Optical fiber
One of embodiments relates to an optical fiber in which an alkali metal element is efficiently doped to its core to suppress transmission loss from increasing. A mean concentration or a concentration distribution of the alkali metal element is adjusted such that 0.48 or less is obtained as an weighted value obtained by weighting a distribution of field intensity of guided light at a wavelength of 1550 nm, with respect to a radial direction distribution of a ratio I D2 /I ω3 of an intensity I D2 of Raman scattering light by a silica three-membered ring structure and an intensity I ω3 of Raman scattering light by a Si—O stretching vibration, in a cross-sectional region having a diameter of 20 μm.
1. An optical fiber mainly comprised of silica-based glass, comprising:
a core extending along an optical axis and including an alkali metal element; and
a cladding surrounding the core and having a refractive index lower than that of the core,
wherein, where an intensity of Raman scattering light ω 3 by a Si—O stretching vibration in a Raman scattering spectrum is I ω3 and an intensity of Raman scattering light D 2 by a silica three-membered ring structure is I D2 , a mean concentration of the alkali metal element in the core or a shape of a concentration distribution of the alkali metal element in the core is adjusted such that 0.48 or less is obtained as a weighted value of a distribution of a ratio I D2 /I ω3 along the radial direction of the optical fiber, the weighted value being obtained by weighting the distribution of the ratio I D2 /I ω3 with a distribution of field intensity along a radial direction of guided light at a wavelength of 1550 nm, calculated from a refractive index profile along the radial direction of the optical fiber, in a region including the optical axis as a center and having a diameter of 20 μm in a cross section of the optical fiber orthogonal to the optical axis.
2. The optical fiber according to claim 1 , wherein
the alkali metal element includes potassium.
3. The optical fiber according to claim 1 , wherein
the concentration distribution of the alkali metal element, in the cross section of the optical fiber orthogonal to the optical axis, has a shape in which a first concentration peak is located in an annular region surrounding the optical axis in a state in which the annular region is separated by a predetermined distance from the optical axis.
4. The optical fiber according to claim 3 , wherein
the concentration distribution of the alkali metal element, in the cross section of the optical fiber orthogonal to the optical axis, has a shape in which a second concentration peak, having a maximum concentration lower than a maximum concentration of the first concentration peak, is located in a region surrounded by the annular region.
5. The optical fiber according to claim 1 , wherein
the concentration distribution of the alkali metal element, in the cross section of the optical fiber orthogonal to the optical axis, has a shape in which there are a plurality of concentration peaks separated from each other along the radial direction of the optical fiber, and
a maximum concentration of one concentration peak close to the optical axis in two adjacent concentration peaks included in the plurality of concentration peaks is lower than a maximum concentration of the other concentration peak in the two adjacent concentration peaks.
6. An optical fiber mainly comprised of silica-based glass, comprising:
a core extending along an optical axis and including an alkali metal element; and
a cladding surrounding the core and having a refractive index lower than that of the core,
wherein, where an intensity of Raman scattering light ω 3 by a Si—O stretching vibration in a Raman scattering spectrum is I ω3 and an intensity of Raman scattering light D 2 by a silica three-membered ring structure is I D2 , a mean concentration of the alkali metal element in the core or a shape of a concentration distribution of the alkali metal element in the core is adjusted such that 0.50 or less is obtained as a ratio I D2 /I ω3 at a position where a field intensity of guided light at a wavelength of 1550 nm calculated from a refractive index profile along a radial direction of the optical fiber is maximized, in a cross section of the optical fiber orthogonal to the optical axis.
7. The optical fiber according to claim 6 , wherein
the alkali metal element includes potassium.
8. The optical fiber according to claim 6 , wherein
the concentration distribution of the alkali metal element, in the cross section of the optical fiber orthogonal to the optical axis, has a shape in which a first concentration peak is located in an annular region surrounding the optical axis in a state in which the annular region is separated by a predetermined distance from the optical axis.
9. The optical fiber according to claim 8 , wherein
the concentration distribution of the alkali metal element, in the cross section of the optical fiber orthogonal to the optical axis, has a shape in which a second concentration peak, having a maximum concentration lower than a maximum concentration of the first concentration peak, is located in a region surrounded by the annular region.
10. The optical fiber according to claim 6 , wherein
the concentration distribution of the alkali metal element, in the cross section of the optical fiber orthogonal to the optical axis, has a shape in which there are a plurality of concentration peaks separated from each other along the radial direction of the optical fiber, and
a maximum concentration of one concentration peak close to the optical axis in two adjacent concentration peaks included in the plurality of concentration peaks is lower than a maximum concentration of the other concentration peak in the two adjacent concentration peaks.
11. An optical fiber mainly comprised of silica-based glass, comprising:
a core extending along an optical axis and including an alkali metal element; and
a cladding surrounding the core and having a refractive index lower than that of the core,
wherein, where an intensity of Raman scattering light ω 3 by a Si—O stretching vibration in a Raman scattering spectrum is I ω3 and an intensity of Raman scattering light D 2 by a silica three-membered ring structure is I D2 , a mean concentration of the alkali metal element in the core or a shape of a concentration distribution of the alkali metal element in the core is adjusted such that 0.15 or less is obtained as a difference between a value of a ratio I D2 /I ω3 at a position where a field intensity of guided light at a wavelength of 1550 nm calculated from a refractive index profile along a radial direction of the optical fiber is maximized and a value of a ratio I D2 /I ω3 on the optical axis, in a cross section of the optical fiber orthogonal to the optical axis.
12. The optical fiber according to claim 11 , wherein
the alkali metal element includes potassium.
13. The optical fiber according to claim 11 , wherein
the concentration distribution of the alkali metal element, in the cross section of the optical fiber orthogonal to the optical axis, has a shape in which a first concentration peak is located in an annular region surrounding the optical axis in a state in which the annular region is separated by a predetermined distance from the optical axis.
14. The optical fiber according to claim 13 , wherein
the concentration distribution of the alkali metal element, in the cross section of the optical fiber orthogonal to the optical axis, has a shape in which a second concentration peak, having a maximum concentration lower than a maximum concentration of the first concentration peak, is located in a region surrounded by the annular region.
15. The optical fiber according to claim 11 , wherein
the concentration distribution of the alkali metal element, in the cross section of the optical fiber orthogonal to the optical axis, has a shape in which there are a plurality of concentration peaks separated from each other along the radial direction of the optical fiber, and
a maximum concentration of one concentration peak close to the optical axis in two adjacent concentration peaks included in the plurality of concentration peaks is lower than a maximum concentration of the other concentration peak in the two adjacent concentration peaks.