View Patent ↗Existing methods of producing high quality graphene/graphite oxides are generally accomplished by exfoliating graphite into flakes and oxidizing the graphite flakes with strong oxidizers under extreme conditions and require careful purification. The oxidizers are typically strong acids used in high concentrations at elevated temperatures requiring complicated purification processes to yield oxidized graphene/sheets. The existing processes can cost up to $12,000/gram. This invention uses a mild oxidant combined with mechanical processing where the sole products are oxidized graphite/graphene and water without the need for further purification.
1. A method of making graphene oxide, consisting essentially of:
placing graphite into water containing an oxidizing agent, wherein said oxidizing agent is at a concentration at which it has an oxidation potential less than 2V;
mechanically exfoliating the graphite and simultaneously oxidizing the graphite into graphene oxide flakes, wherein the step of mechanically exfoliating graphite into graphene oxide flakes is done in a stirred media mill, and the stirred media mill is an attrition mill, a dry grind attritor, a wet grind attritor, a regular speed attritor, a high speed attritor, or an attritor; and
separating the graphene oxide flakes from the water, wherein the graphene oxide flakes are flat.
2. The method of claim 1 , wherein the oxidizing agent is selected CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3 , ClO 2 , or H 2 O 2 .
3. The method of claim 1 , wherein the oxidizing agent is aqueous or non-aqueous.
4. The method of claim 1 , wherein the pH of the water containing the graphene oxide flakes is from pH 2 to pH 9.
5. The method of claim 1 , wherein the pH of the resulting water graphene oxide flakes mixture is about 7.
6. The method of claim 1 , wherein 1% to 15% of the graphite is oxidized to become graphene oxide flakes.
7. The method of claim 1 , further comprising the step of precipitating any remaining graphite by increasing the pH of the resulting water graphene oxide flakes mixture above pH 9, or by decreasing the pH of the resulting water graphene oxide flakes mixture below a pH of 3.
8. A method of making graphene flakes and graphene oxide flakes, consisting essentially of:
placing graphite into water containing an oxidizing agent, wherein said oxidizing agent is at a concentration at which it has an oxidation potential less than 2V;
mechanically exfoliating graphite and simultaneously oxidizing the graphite into graphene oxide flakes and graphene flakes, wherein the step of mechanically exfoliating graphite into graphene oxide flakes and graphene flakes is done in a stirred media mill, and the stirred media mill is an attrition mill, a dry grind attritor, a wet grind attritor, a regular speed attritor, a high speed attritor, or an attritor; and
separating the graphene flakes and graphene oxide flakes from the water, wherein the graphene flakes and graphene oxide flakes are flat.
9. The method of claim 8 , wherein the oxidizing agent is CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3 , ClO 2 , or H 2 O 2 .
10. The method of claim 8 , wherein the oxidizing agent is aqueous or non-aqueous.
11. The method of claim 8 , wherein the pH of the water containing the graphene flakes and graphene oxide flakes is from pH 2 to pH 9.
12. The method of claim 8 , wherein the pH of the resulting water graphene flakes and graphene oxide flakes mixture is about 7.
13. The method of claim 8 , wherein 1% to 15% of the graphite is oxidized to become the graphene oxide flakes.
14. The method of claim 8 , further comprising the step of precipitating any remaining graphite by increasing the pH of the resulting water, graphene oxide flakes, and graphene flakes mixture above pH 9 or by decreasing the pH of the resulting water, graphene oxide flakes, and graphene flakes mixture below a pH of 3.