Composite floor and manufacturing method thereof
View Patent ↗The present invention provides a composite floor and a manufacturing method thereof. The composite floor comprises a coextrusion layer compression moulded by a coextrusion process. The coextrusion layer comprises a first PVC (polyvinyl chloride) equilibrium layer, a WPC (Wood/Plastic Composite) foaming layer, and a second PVC equilibrium layer sequentially arranged from top to bottom. In the composite floor of this invention, the WPC foaming layer is the main material layer, and thus the whole weight of the floor is reduced. The first PVC equilibrium layer and the second PVC equilibrium layer are arranged respectively at two sides of the WPC foaming layer so that the composite floor is more stable in performance. It is more friendly to environment and simple in manufacturing procedure to adopt the coextrusion process for compression moulding because of avoiding bonding using glue.
1. A manufacturing method of a composite floor, comprising following steps:
S1: respectively mixing raw materials of PVC equilibrium layers and raw materials of a WPC foaming layer;
S2: extruding the raw materials of the WPC foaming layer into a layer, and extruding the raw materials of the PVC equilibrium layers into two layers, namely a first PVC equilibrium layer and a second PVC equilibrium layer, wherein the first PVC equilibrium layer is extruded on the WPC foaming layer, the second PVC equilibrium layer is extruded beneath the WPC foaming layer, and the first PVC equilibrium layer, the WPC foaming layer, and the second PVC equilibrium layer form a coextrusion layer semi-finished product; and
S3: moving the coextrusion layer semi-finished product to be between a pair of oppositely-arranged pressing rollers for compression moulding, a temperature of the pressing rollers ranging from 180° C. to 210° C., and a space between the pair of pressing rollers being 0.7 mm-1.3 mm subtracted from a thickness of the coextrusion layer semi-finished product;
wherein a movement speed of the coextrusion layer semi-finished product ranges from 0.5 m/min to 1.5 m/min.
2. The manufacturing method according to claim 1 , wherein the Step S1 further comprises preheating the mixed raw materials of the PVC equilibrium layers to 170° C.-190° C., and preheating the mixed raw materials of the WPC foaming layer to 170° C.-190° C.
3. The manufacturing method according to claim 1 , wherein the Step S1 further comprises mixing raw materials of a mute layer; and the Step S2 further comprises extruding the raw materials of the mute layer to be beneath the second PVC equilibrium layer, wherein the mute layer, the first PVC equilibrium layer, the WPC foaming layer, and the second PVC equilibrium layer form the coextrusion layer semi-finished product.
4. The manufacturing method according to claim 1 , wherein the PVC equilibrium layers are made from following raw materials of parts by weight: PVC 20-30 parts by weight, calcium carbonate 65-75 parts by weight, calcium-zinc stabilizer 1-3 parts by weight, chlorinated polyethylene 1-3 parts by weight, acrylic ester 0.5-1.5 parts by weight, PE-wax 0.1-0.5 parts by weight, stearic acid 0.1-0.5 parts by weight, and carbon black 0.1-0.5 parts by weight; and the WPC foaming layer is made from following raw materials of parts by weight: polyvinyl chloride 35-55 parts by weight, stone powder 40-50 parts by weight, calcium-zinc stabilizer 2-3 parts by weight, internal lubricant for PVC 0.2-0.6 parts by weight, external lubricant for PVC 0.1-0.4 parts by weight, acrylic ester 3-5 parts by weight, oxidized polyethylene homopolymer 0.1-0.4 parts by weight, sodium bicarbonate 0.1-0.4 parts by weight, 2,2-azobisisobutyronitrile 0.1-0.4 parts by weight, and chlorinated polyvinyl chloride 1-2 parts by weight.
5. The manufacturing method according to claim 1 , wherein the WPC foaming layer is made from following raw materials of parts by weight: polyvinyl chloride 35-55 parts by weight, stone powder 40-50 parts by weight, calcium-zinc stabilizer 2-3 parts by weight, internal lubricant for PVC 0.2-0.6 parts by weight, external lubricant for PVC 0.1-0.4 parts by weight, acrylic ester 3-5 parts by weight, oxidized polyethylene homopolymer 0.1-0.4 parts by weight, sodium bicarbonate 0.1-0.4 parts by weight, 2,2-azobisisobutyronitrile 0.1-0.4 parts by weight and chlorinated polyvinyl chloride 1-2 parts by weight.
6. A manufacturing method of a composite floor, comprising following steps:
S1: respectively mixing raw materials of PVC equilibrium layers and raw materials of a WPC foaming layer;
S2: extruding the raw materials of the WPC foaming layer into a layer, and extruding the raw materials of the PVC equilibrium layers into two layers, namely a first PVC equilibrium layer and a second PVC equilibrium layer, wherein the first PVC equilibrium layer is extruded on the WPC foaming layer, the second PVC equilibrium layer is extruded beneath the WPC foaming layer, and the first PVC equilibrium layer, the WPC foaming layer, and the second PVC equilibrium layer form a coextrusion layer semi-finished product; and
S3: moving the coextrusion layer semi-finished product to be between a pair of oppositely-arranged pressing rollers for compression moulding, a temperature of the pressing rollers ranging from 180° C. to 210° C., and a space between the pair of pressing rollers being 0.7 mm-1.3 mm subtracted from a thickness of the coextrusion layer semi-finished product;
wherein the Step S1 further comprises preheating the mixed raw materials of the PVC equilibrium layers to 170° C.-190° C., and preheating the mixed raw materials of the WPC foaming layer to 170° C.-190° C.
7. A manufacturing method of a composite floor, comprising following steps:
S1: respectively mixing raw materials of PVC equilibrium layers and raw materials of a WPC foaming layer;
S2: extruding the raw materials of the WPC foaming layer into a layer, and extruding the raw materials of the PVC equilibrium layers into two layers, namely a first PVC equilibrium layer and a second PVC equilibrium layer, wherein the first PVC equilibrium layer is extruded on the WPC foaming layer, the second PVC equilibrium layer is extruded beneath the WPC foaming layer, and the first PVC equilibrium layer, the WPC foaming layer, and the second PVC equilibrium layer form a coextrusion layer semi-finished product; and
S3: moving the coextrusion layer semi-finished product to be between a pair of oppositely-arranged pressing rollers for compression moulding, a temperature of the pressing rollers ranging from 180° C. to 210° C., and a space between the pair of pressing rollers being 0.7 mm-1.3 mm subtracted from a thickness of the coextrusion layer semi-finished product;
wherein the Step S1 further comprises mixing raw materials of a mute layer; and the Step S2 further comprises extruding the raw materials of the mute layer to be beneath the second PVC equilibrium layer, wherein the mute layer, the first PVC equilibrium layer, the WPC foaming layer, and the second PVC equilibrium layer form the coextrusion layer semi-finished product.