Carbon dioxide reduction electro catalysts prepared for metal organic frameworks
View Patent ↗A pyrolyzed MOF catalyst for in the carbon dioxide reduction reaction and methods of making the catalyst. The catalysts are composed of highly porous transition metal organic frameworks exhibiting large pores with regular distribution of transition metals within the structure.
1. A method comprising:
preparing a metal organic framework by:
reacting a nitrogen-free organic ligand with a transition metal ion, the transition metal ion comprising copper; and
modifying the metal organic framework by:
pyrolyzing the metal organic framework at a temperature between 800° C. and 810° C. for a period between 60 minutes and 120 minutes;
forming micropores, during the pyrolyzing, within the pyrolyzed metal organic framework; and
forming, during the pyrolyzing, a transition metal microcrystallite within at least a portion of the micropores, the transition metal microcrystallite being in a zero valance state;
wherein the transition metal microcrystallites comprise at least a 3:1 ratio of copper (111) facets to copper (200) facets and the modified metal organic framework has an average pore diameters ranging from 10 to 15 angstroms.
2. The method of claim 1 , wherein the organic ligand is selected from the group consisting of: 1,4-dicarboxylic acid, and 1,3,5 tricarboxylic acid.
3. The method of claim 1 further forming the metal organic framework further comprises replacing a portion of the transition metal reacted with the organic ligand with a second transition metal wherein a multi-metallic metal organic framework is formed.
4. The method of claim 1 , wherein the metal microcrystallites have a size range of 10 nm to 10 μm.