Ceramic material, method for producing the ceramic material, and electroceramic component comprising the ceramic material

1. A ceramic material, comprising lead zirconate titanate, which additionally contains Nd, and K, according to the following formula:

Pb 1-(3x/2)-a Nd x K 2a V Pb(x/2)-a (Zr 1-y Ti y )O 3 ,

within the limits 0.0001≤x≤0.06, 0.0001≤a≤0.03, 0.35≤y≤0.60, preferably in the composition range.

2. The ceramic material according to claim 1 , in which the lead zirconate titanate has the general composition ABO 3 of a perovskite lattice, wherein A represents the A sites and B represents the B sites of the perovskite lattice and Nd, and K occupy A sites in the perovskite lattice.

3. An electroceramic component comprising a ceramic material according to claim 1 or 2 .

4. The electroceramic component according to claim 3 , in the form of a piezoelectric actuator.

5. The piezoelectric actuator according to claim 4 , comprising:

at least two layers of the ceramic material; and

an inner electrode, preferably a Cu inner electrode, between the at least two layers.

6. A method for producing a ceramic material according to claim 1 or 2 , comprising the following steps:

A) producing a ceramic raw material mixture by comminuting and mixing starting materials containing Pb, Zr, Ti, Nd and oxygen;

B) introducing a K-containing compound;

C) calcining the raw material mixture; and

D) sintering to form the ceramic.

7. The method according to claim 6 , wherein an additional method step A1), in which the ceramic raw material mixture is calcined and then comminuted, is carried out after method step A) and before method step B).

8. The method according to claim 6 , wherein Nd is added in a range of from 0.01 to 6 mol %.

9. The method according to claim 6 , wherein a K-containing compound is introduced before the calcining in method step C).

10. The method according to claim 6 , wherein a K-containing compound is introduced after the calcining in method step C).

11. The method according to claim 6 , wherein an additional method step C1), in which the calcined ceramic raw material mixture is comminuted and mixed with up to 1.5 mol % PbO, is carried out after method step C) and before method step D).

12. The method according to claim 6 , wherein K are added in a range of from 0.01 to 6 mol %.

13. The method according to claim 6 , wherein, before method step D), ceramic green sheets are formed from the ceramic raw material mixture comprising a binder.

14. A method for producing a multilayer component, comprising:

A) producing a first ceramic raw material mixture by comminuting and mixing starting materials containing Pb, Zr, Ti, Nd and oxygen;

B) calcining the first ceramic raw material mixture;

C) comminuting the calcined first ceramic raw material mixture and mixing with a K-containing compound to produce a second ceramic raw material mixture;

D) calcining the second ceramic raw material mixture;

E) adding a binder to the ceramic raw material mixture of D;

F) forming green sheets from the mixture of E;

G) printing inner electrodes on the green sheets of F, the material of the inner electrodes comprising Cu,

H) layering a multiplicity of the ceramic green sheets of G on top of one another to form a stack;

I) consolidating the stack by lamination, as a result of which green parts are formed;

J) debindering the green parts; and

K) sintering the green parts, some of the Cu being transferred from the inner electrodes into the ceramic material and being incorporated therein.

15. The method according to claim 14 , wherein the material of the inner electrodes comprises metallic Cu or Cu oxide.