Method of making optical fibers with multiple openings
A method of making an optical fiber with multiple openings comprising the steps of fabricating an extrusion die using additive manufacturing such that the extrusion die has a plurality of channels that combine inside the die into another set of channels, extruding a glass, forming a fiber optic preform having a plurality of longitudinal openings that run the entire length, attaching a barrier layer for pressure application, and stretching the preform into an optical fiber with multiple openings. An extrusion die comprising an additive manufactured material, having a proximal side having openings and having a distal side having openings, wherein the openings of the proximal side are of feed channels, wherein the openings of the distal side are of forming channels, and wherein in side the body of the die, two of the feed channels combine the forming channels.
1. A method of making an optical fiber with multiple openings, comprising the steps of:
fabricating an extrusion die using at least one additive manufacturing technique such that the extrusion die has a first set of plurality of channels that combine inside the die into a second set of plurality of channels with a different set of shapes and sizes;
extruding a glass through the extrusion die;
forming a fiber optic preform having a plurality of longitudinal openings that run the entire length of the fiber optic preform;
attaching a barrier layer to the fiber optic preform to form a series of channels to which pressure can be applied by a gas;
wherein each channel has a pressure that is independently controlled; and
stretching the fiber optic preform at an elevated temperature into an optical fiber with multiple openings.
2. The method of making an optical fiber with multiple openings of claim 1 , wherein the step of extruding comprises softening the glass to reach a viscosity in the range of 10 11 to 10 6 Pa*sec.
3. The method of making an optical fiber with multiple openings of claim 1 , wherein the step of extruding comprises softening the glass to reach a viscosity in the range of 10 8 to 10 10 Pa*sec.
4. The method of making an optical fiber with multiple openings of claim 1 , wherein the step of stretching comprises heating the fiber optic preform such that the viscosity of the fiber optic preform reaches 10 7 to 10 3 Pa*sec.
5. The method of making an optical fiber with multiple openings of claim 1 , wherein the step of stretching comprises heating the fiber optic preform such that the viscosity of the fiber optic preform reaches 10 5 to 10 6 Pa*sec.
6. A method of making an optical fiber with multiple openings, comprising the steps of:
designing a fiber structure;
designing and fabricating an extrusion die using additive manufacturing or three-dimensional (3D) printing;
wherein the extrusion die has a first set of plurality of channels that combine inside the die into a second set of plurality of channels with a different set of shapes and sizes;
wherein each channel has a pressure that is independently controlled;
extruding a preform from an IR-transparent glass from the additive-manufactured die; and
stretching the preform into an optical fiber with multiple openings.
7. The method of making an optical fiber with multiple openings of claim 6
wherein the IR-transparent glass is softened.
8. The method of making an optical fiber with multiple openings of claim 6 , further comprising the steps of:
heating the IR-transparent glass prior to the step of extruding a preform, wherein said heating the IR-transparent glass comprising heating to a temperature of about 350° C. for about 10 hours.
9. The method of making an optical fiber with multiple openings of claim 6 , wherein the step of extruding comprises softening the glass to reach a viscosity in the range of 10 11 to 10 6 Pa*sec.
10. The method of making an optical fiber with multiple openings of claim 6 , wherein the step of stretching comprises heating the fiber optic preform such that the viscosity of the fiber optic preform reaches 10 7 to 10 3 Pa*sec.