Method for manufacturing a mechanical component

1. A method for manufacturing a mechanical component, the method comprising:

additively manufacturing at least one layering sequence of depositing a powder material and locally melting and resolidifying the powder material, wherein in each layering sequence a solid layer of solidified material is formed, wherein plural solid layers jointly form a solid body;

executing an annealing sequence subsequent to at least one layering sequence, the annealing sequence including locally heating at least a region of the solid body in effecting a local heat input to an immediately beforehand manufactured solid layer which was formed by an immediately precedent layering sequence, wherein a material temperature during the annealing sequence is maintained below a melting temperature of the material;

controlling a heat input per unit area during the annealing sequence such as to heat part of the solid body to a first temperature range and maintain temperature within said first temperature range for a dwell time; and

selecting the first temperature range such that a lower boundary value of the first temperature range is higher than a threshold temperature for gamma prime phase precipitation, and an upper boundary value of the first temperature range is lower than a melting point of the resolidified material.

2. The method according to claim 1 , wherein locally melting the powder material comprises:

exposing the powder material to radiation at a first incident radiation intensity and providing a first incident radiation energy per unit area; and locally heating at least a part of the solid body comprises:

exposing the immediately beforehand manufactured solid layer to radiation at a second incident radiation intensity and providing a second incident radiation energy per unit area.

3. The method according to claim 2 , wherein the second incident radiation intensity is smaller than the first incident radiation intensity by at least one order of magnitude.

4. The method according to claim 2 , wherein the second incident energy provided per unit area is smaller than the first incident energy provided per unit area.

5. The method according to claim 2 , wherein locally melting the powder material comprises:

projecting a beam of radiation of a first radiation power onto a first projection surface on the powder material; and locally heating at least a part of the solid body comprises:

projecting a beam of radiation of a second power onto a second projection surface on the immediately beforehand manufactured solid layer, wherein the second projection surface is larger than the first projection surface.

6. The method according to claim 2 , wherein locally melting the powder material comprises:

moving a projection location of a beam of radiation over the powder material surface at a first scan speed: and locally heating at least a part of the solid body comprises:

moving a projection location of a beam of radiation over a surface of the immediately beforehand manufactured solid layer at a second scan speed, wherein the second scan speed is larger than the first scan speed.

7. The method according to claim 1 , comprising:

controlling heat input to achieve a temperature gradient to reach the first temperature range before the precipitation of a gamma prime phase sets in.

8. The method according to claim 1 , comprising:

performing a multitude of subsequent layering sequences, and performing an annealing sequence between two consecutive layering sequences.

9. The method according to claim 8 , comprising:

performing at least two consecutive layering sequences without an intermediate annealing sequence.

10. The method according to claim 9 , comprising:

performing an annealing sequence subsequent to every n th layering sequence, wherein n>2.

11. The method according to claim 8 , comprising:

performing an annealing sequence subsequent to at least one layering sequence in which solid layers are formed only in specific regions of the component to be built.

12. The method according to claim 1 , wherein an annealing sequence comprises:

effecting a local heat input to at least essentially an entire cross sectional surface of the preceding manufactured solid layer.

13. The method according to claim 1 , wherein an annealing sequence comprises:

effecting a local heat input to only selected partial areas of a cross sectional surface of the preceding manufactured solid layer.