Nanowire bundle and method of manufacturing nanostructure
A method of manufacturing a nanostructure includes: heating a mixed solution to a first temperature, the mixed solution including a solvent, a compound including indium, and an octadecylphosphonic acid; heating the mixed solution to a second temperature; injecting, after heating the mixed solution to the second temperature, a phosphine precursor into the mixed solution; and heating the mixed solution including the injected phosphine precursor to a third temperature.
1. A method of manufacturing a nanostructure, the method comprising:
heating a mixed solution to a first temperature, the mixed solution comprising a solvent, a compound comprising indium, and an octadecylphosphonic acid;
heating the mixed solution to a second temperature;
injecting, after heating the mixed solution to the second temperature, a phosphine precursor into the mixed solution; and
heating the mixed solution comprising the injected phosphine precursor to a third temperature.
2. The method of claim 1 , wherein the compound comprising indium represents a compound comprising trivalent indium.
3. The method of claim 2 , wherein the compound comprising trivalent indium is at least one of indium acetate and indium chloride.
4. The method of claim 1 , wherein:
the solvent comprises a hydrocarbon compound; and
a boiling point of the hydrocarbon compound is greater than or equal to 250° C. and less than or equal to 350° C.
5. The method of claim 1 , wherein the phosphine precursor comprises tris(trimethylsilyl)phosphine (P(SiCH 3 ) 3 .
6. The method of claim 1 , wherein heating the mixed solution to the second temperature and injecting the phosphine precursor causes, at least in part, a mole ratio of indium:octadecylphosphonic acid:phosphorus in the mixed solution to be 1:3-5:4-6.
7. The method of claim 1 , wherein heating the mixed solution to the first temperature comprises forming an indium-octadecylphosphonic acid complex compound.
8. The method of claim 7 , wherein heating the mixed solution to the second temperature and injecting the phosphine precursor comprises forming an indium phosphide core.
9. The method of claim 8 , wherein heating the mixed solution comprising the injected phosphine precursor to the third temperature comprises growing the indium phosphide core with the indium-octadecylphosphonic acid complex compound as a template.
10. The method of claim 1 , wherein:
the first temperature is greater than or equal to 280° C. and less than or equal to 320° C.;
the second temperature is greater than or equal to 100° C. and less than or equal to 140° C.; and
the third temperature is greater than or equal to 280° C. and less than or equal to 320° C.
11. The method of claim 10 , wherein, after heating the mixed solution comprising the injected phosphine precursor to the third temperature, the third temperature is maintained for greater than or equal to 50 minutes and less than or equal to 70 minutes.
12. The method of claim 10 , wherein:
the nanostructure is a nanorod; and
an aspect ratio of the nanorod is greater than or equal to 5 and less than or equal to 30.
13. The method of claim 1 , wherein:
the first temperature is greater than or equal to 280° C. and less than or equal to 320° C.;
the second temperature is greater than or equal to 280° C. and less than or equal to 320° C.; and
the third temperature is greater than or equal to 280° C. and less than or equal to 320° C.
14. The method of claim 13 , wherein, after heating the mixed solution comprising the injected phosphine precursor to the third temperature, the third temperature is maintained for greater than or equal to 20 minutes and less than or equal to 40 minutes.
15. The method of claim 13 , wherein:
the nanostructure is a nanowire; and
an aspect ratio of the nanowire is greater than or equal to 40 and less than or equal to 200.
16. The method of claim 1 , wherein:
the first temperature is greater than or equal to 280° C. and less than or equal to 320° C.;
the second temperature is greater than or equal to 180° C. and less than or equal to 220° C.; and
the third temperature is greater than or equal to 180° C. and less than or equal to 320° C.
17. The method of claim 16 , wherein, after heating the mixed solution comprising the injected phosphine precursor to the third temperature, the third temperature is maintained for greater than or equal to 10 seconds and less than or equal to 7 minutes.
18. The method of claim 16 , wherein:
the nanostructure is a nanowire bundle;
the nanowire bundle is a combination of at least ten nanowires; and
an aspect ratio of each nanowire of the at least ten nanowires is greater than or equal to 40 and less than or equal to 200.
19. A nanowire bundle comprising:
an indium-octadecylphosphonic acid template;
a first indium phosphide nanowire; and
a second indium phosphide nanowire combined and arranged in a one dimensional manner with the first indium phosphide nanowire via the indium-octadecylphosphonic acid template.
20. The nanowire bundle of claim 19 , wherein a width of the nanowire bundle is greater than or equal to 30 nm and less than or equal to 200 nm.