SCR catalyst for removing nitrogen oxides and method for producing same
A SCR catalyst for removing nitrogen oxides comprises: a carrier prepared from a support in which Ti-PILC is mixed with titania; and a catalyst material on the carrier, wherein the catalyst material contains an active material of a vanadium component and a co-catalyst of a tungsten component. On the basis of the total weight of the catalyst, the support Ti-PILC is contained at 0.01-40 wt %, and the support titania is contained at 50 to 90 wt %. In addition, a method for producing a SCR catalyst for removing nitrogen oxides comprises the steps of: preparing a carrier by using a support in which Ti-PILC is mixed with titania; and supporting a catalyst material on the carrier. The present disclosure provides: a SCR catalyst for removing nitrogen oxides, which has an excellent nitrogen oxide removing performance and a high producing convenience; and a method for producing the same.
1. A SCR catalyst for removing nitrogen oxides, comprising a support in which Ti-pillared interlayer clay (Ti-PILC) is mixed with titania (TiO 2 ) as a carrier, wherein, on the basis of a total weight of the catalyst, the ratio of the support Ti-PILC to the support titania (TiO 2 ) is 0.1 to 0.4.
2. The SCR catalyst for removing nitrogen oxides according to claim 1 , wherein a catalyst material on the carrier contains an active material of a vanadium (V 2 O 5 ) component and a cocatalyst of a tungsten (WO 3 ) component.
3. The SCR catalyst for removing nitrogen oxides according to claim 2 , wherein on the basis of the total weight of the catalyst, the active material vanadium (V 2 O 5 ) is contained at 0.01-15 wt %, and the cocatalyst tungsten (WO 3 ) is contained at 0.01 to 15 wt %.
4. The SCR catalyst for removing nitrogen oxides according to claim 1 , wherein to the catalyst, a cocatalyst selected from a group consisting of cerium (Ce), sulfur dioxide (SO 2 ), iron (Fe), molybdenum (Mo), yttrium (Y), and lanthanides is further added at 10 wt % or less with respect to the total weight of the catalyst.
5. A method for producing a SCR catalyst for removing nitrogen oxides, the method comprising the steps of:
preparing a carrier by using a support in which Ti-pillared interlayer clay (Ti-PILC) is mixed with titania (TiO 2 ) wherein, on the basis of a total weight of the catalyst, the ratio of the support Ti-PILC to the support titanic (TiO 2 ) is 0.1 to 0.4; and supporting a catalyst material on the carrier.
6. The method according to claim 5 , wherein the supporting step supports a catalyst material comprising the active material vanadium (V 2 O 5 ) and the cocatalyst tungsten (WO 3 ).
7. The method according to claim 5 , wherein to the catalyst, a cocatalyst selected from a group consisting of cerium (Ce), sulfur dioxide (SO 2 ), iron (Fe), molybdenum (Mo), yttrium (Y), and lanthanides is further added in the supporting step.
8. The method according to claim 5 , wherein calcination is performed at a calcination temperature of 500° C. to 600° C. after the supporting.
9. The SCR catalyst for removing nitrogen oxides according to claim 1 , wherein, on the basis of the total weight of the catalyst, the ratio of the support Ti-PILC to the support titania (TiO 2 ) is 0.25.
10. The method according to claim 5 , wherein, on the basis of the total weight of the catalyst, the ratio of the support Ti-PILC to the support titania (TiO 2 ) is 0.25.