Cementitious material for radioactive waste disposal facility
The cementitious material for a radioactive waste disposal facility includes base cement, and porous and amorphous silica powder. The amount of the silica powder in the entire cementitious material ranges from 35% to 65% on a mass basis.
1. A cementitious material for a radioactive waste disposal facility comprising:
base cement; and porous and amorphous silica powder, wherein
the amount of the silica powder in the entire cementitious material ranges from 35% to 65% on a mass basis,
the silica powder has an average particle diameter ranging from 3 μm to 7 μm, and
in a particle size distribution of the silica powder, an amount of particles larger than 10 μm is 15% or less in the entire silica powder, and an amount of particles smaller than 1 μm is 6% or less.
2. The cementitious material for a radioactive waste disposal facility according to claim 1 , wherein
the silica powder contains an alkaline oxide, and
a total alkaline oxide content in the entire silica powder is 4.1% or lower on a mass basis.
3. The cementitious material for a radioactive waste disposal facility according to claim 1 , wherein
the silica powder has a silica purity of 93% or higher on a mass basis.
4. The cementitious material for a radioactive waste disposal facility according to claim 1 , wherein
the silica powder is made by pulverizing ash of burnt plant material.
5. The cementitious based material for a radioactive waste disposal facility according to claim 1 , wherein
the silica powder is ash made by soaking a plant material in an acid solution and then burning the plant material.
6. The cementitious material for a radioactive waste disposal facility according to claim 4 , wherein
the plant material is rice husk.
7. The cementitious material for a radioactive waste disposal facility according to claim 2 , wherein
the alkaline oxide includes one or more oxides selected from the group consisting of sodium oxide, potassium oxide, calcium oxide, and magnesium oxide.
8. The cementitious material for a radioactive waste disposal facility according to claim 1 , wherein
the cementitious material is a grouting material for the radioactive waste disposal facility, the grouting material comprising a grouting material powder containing the base cement mixed with the silica powder.
9. The cementitious material for a radioactive waste disposal facility according to claim 8 , wherein
the grouting material powder has an average particle diameter ranging from 3 μm to 7 μm, and
in a particle size distribution of the grouting material powder, an amount of particles larger than 10 μm is 15% or less in the entire grouting material, and an amount of particles smaller than 1 μm is 6% or less.