Composition of catalysts for conversion of ethanol to N-butanol and higher alcohols
A method of producing a catalyst can include heating a hydrotalcite above a decomposition temperature, forming a decomposed hydrotalcite in response to the heating, combining the decomposed hydrotalcite with a metal salt to form a catalyst mixture, and heating the catalyst mixture to convert the metal salt to a metal oxide. The resulting metal oxide combined with the decomposed hydrotalcite forms the catalyst.
1. A method for producing a higher alcohol comprising:
contacting a reactant comprising ethanol with a catalyst at a reaction temperature and pressure sufficient to produce a reaction product,
wherein the catalyst comprises: 1) a thermally decomposed hydrocalumite mixed with one or more metal oxides, or 2) a combination of a thermally decomposed hydrocalumite and a thermally decomposed hydrotalcite mixed with one or more metal oxides, wherein the reaction product comprises a higher alcohol.
2. The method of claim 1 , wherein the higher alcohol is butanol.
3. The method of claim 1 , wherein the higher alcohol comprises a C 4 -C 13 alcohol.
4. The method of claim 1 , wherein a conversion of ethanol to the higher alcohol is at least about 10%.
5. The method of claim 1 , wherein a selectivity of the conversion of ethanol to the higher alcohol is at least about 90%.
6. The method of claim 1 , wherein the one or more metal oxides comprise one or more metals selected from the group consisting of: Pd, Cu, Pt, Cr, Ni, Fe, Ru, Rh, and Co.
7. The method of claim 1 , wherein the one or more metal oxides comprises an alkaline salt, an alkaline earth salt, or any combination thereof.
8. The method of claim 1 , wherein the catalyst has a surface of between about 20 m 2 /g to about 100 m 2 /g.
9. The method of claim 1 , wherein the catalyst has a pore volume of between about 0.05 cm 3 /g and about 0.4 cm 3 /g.
10. The method of claim 1 , wherein the catalyst further comprises a support material.
11. A reactive distillation method comprising:
introducing a feed stream to a reactive distillation system, wherein the feed stream comprises one or more alpha hydrogen alcohols;
contacting the feed stream with at least one catalyst during a distillation, wherein the feed stream reacts in the presence of the at least one catalyst to produce a reaction product comprising one or more higher alcohols, wherein the catalyst comprises 1) a thermally decomposed hydrocalumite mixed with one or more metal oxides, or 2) a combination of a thermally decomposed hydrocalumite and a thermally decomposed hydrotalcite mized with one or more metal oxides; and
removing the higher alcohols during the distillation from the reactive distillation system as a bottoms stream.
12. The method of claim 11 , wherein the one or more alpha hydrogen alcohols comprise one or more of ethanol, propanol, or butanol.
13. The method of claim 11 , wherein the one or more higher alcohols comprise a C 6 -C 13 alcohol.
14. The method of claim 11 , wherein the one or more higher alcohols comprise at least one alcohol selected from the group consisting of: 1-hexanol, 2-ethyl-1-butanol, 1-octanol, 2-ethyl-2-hexanol, heptanol, decanol, and dodecanols.
15. The method of claim 11 , further comprising: converting at least a portion of the higher alcohols to one or more ethers.
16. The method of claim 11 , wherein the reactive distillation system comprises a reactive distillation column, and wherein contacting the feed stream with the at least one catalyst during the distillation comprises contacting the feed stream with the at least one catalyst in one or more side reactors in fluid communication with the reactive distillation column.
17. The method of claim 16 , wherein the feed stream is introduced into the reactive distillation column.
18. The method of claim 16 , wherein the feed stream is introduced into at least one of the one or more side reactors.
19. The method of claim 1 , wherein the catalyst comprises;
a first material having a formula:
(M 2+ x M 3+ y (OH) (2x+3y) )
wherein the M 2+ ions comprise one or more of Mg, Ni, Pt, Pd, Zn, Co, Fe, or Cu, wherein the M 3+ ions comprise at least one of Al, Fe, or Cr, wherein x is in the range of from 2 to 7, wherein y is in the range of from 1.5 to 2.5; and
one or more second materials comprising at least one of Pt, Pd, Cu, Cr 2 O 3 , CuCr 2 O 5 , Ni, Fe, Ru, Rh, Ir, Os, or Co.
20. The method of claim 19 , wherein the first material comprises meixnerite (Mg 6 Al 2 (OH) 18 .4H 2 O).
21. The method of claim 1 , wherein the catalyst comprises:
a first material having a formula:
(M 2+ x M 3+ y O (x+1.5y) )
wherein the M 2+ ions comprise one or more of Mg, Ni, Pt, Pd, Zn, Co, Fe, or Cu, wherein the M 3+ ions comprise at least one of Al, Fe, or Cr, wherein x is in the range of from 0.5 to 1.5, wherein y is in the range of from 1.5 to 4; and
one or more second materials comprising at least one of Pt, Pd, Cu, Cr2O3, Ni, Fe, Ru, Rh, Ir, or Co.
22. The method of claim 21 , wherein the first material comprises a magnesium aluminum spinel (MgAl 2 O 4 ).
23. The method of claim 1 , wherein the one or more second materials comprise Pd.
24. The method of claim 1 , wherein the one or more second materials comprise Cu.
25. The method of claim 1 , where the loading of the one or more second materials is between about 0.01 wt % and about 5 wt. %.
26. The method of claim 11 , wherein the catalyst comprises;
a first material having a formula:
(M 2+ x M 3+ y (OH) (2x+3y) )
wherein the M 2+ ions comprise one or more of Mg, Ni, Pt, Pd, Zn, Co, Fe, or Cu, wherein the M 3+ ions comprise at least one of Al, Fe, or Cr, wherein x is in the range of from 2 to 7, wherein y is in the range of from 1.5 to 2.5; and
one or more second materials comprising at least one of Pt, Pd, Cu, Cr 2 O 3 , CuCr 2 O 5 , Ni, Fe, Ru, Rh, Ir, Os, or Co.
27. The method of claim 11 , wherein the catalyst comprises:
a first material having a formula:
(M 2+ x M 3+ y O (x+1.5y) )
wherein the M 2+ ions comprise one or more of Mg, Ni, Pt, Pd, Zn, Co, Fe, or Cu, wherein the M 3+ ions comprise at least one of Al, Fe, or Cr, wherein x is in the range of from 0.5 to 1.5, wherein y is in the range of from 1.5 to 4; and
one or more second materials comprising at least one of Pt, Pd, Cu, Cr2O3, Ni, Fe, Ru, Rh, Ir, or Co.