Cathode active material for lithium ion secondary batteries, method for manufacturing the same, and lithium ion secondary batteries including the same
View Patent ↗Provided is a composite cathode active material including: a core including a lithium transition metal oxide, the lithium transition metal oxide being doped with nickel (Ni) and at least one element selected from Group 4 to Group 13 elements and having a layered crystalline phase belonging to the Space Group R-3m; and a coating layer on a surface of the core, the coating layer including a cobalt compound.
1. A composite cathode active material comprising:
a core comprising a lithium transition metal oxide represented by Formula 3 and having a layered crystalline phase belonging to the Space Group R-3m; and
a coating layer on a surface of the core, the coating layer comprising a cobalt compound:
Li x Co 1-y-q-r Ni y M3 q M4 r O 2 <Formula 3>
wherein, in Formula 3, 1.00≤x≤1.04, 0.05≤y≤0.1, 0<q<0.005, 0<r<0.005, 0.001≤q+r≤0.007, and M3 and M4 are different from one another and are each independently selected from magnesium (Mg), and titanium (Ti).
2. The composite cathode active material of claim 1 , wherein the core comprising the lithium transition metal oxide is a single crystal, and the Ni is located at an octahedral site in the single crystal.
3. The composite cathode active material of claim 1 , wherein a content of Co in M1 in the lithium transition metal oxide represented by Formula 1 is the largest among the elements in M1.
4. The composite cathode active material of claim 1 , wherein a ratio of moles of Li to total moles of Co and Ni (Li/(Co+Ni)) in the lithium transition metal oxide satisfies 1≤Li/(Co+Ni)≤1.04.
5. The composite cathode active material of claim 1 , wherein a rock salt structure is on a surface of the core, the rock salt structure having a thickness of about 5 nm to about 10 nm and belonging to the Space Group Fm-3m.
6. The composite cathode active material of claim 1 , wherein the core of the composite cathode active material has an average particle diameter of about 0.5 μm to about 25 μm.
7. The composite cathode active material of claim 1 , wherein a content of the cobalt compound in the coating layer is about 0.5 parts to about 5.0 parts by weight with respect to 100 parts by weight of the composite cathode active material.
8. The composite cathode active material of claim 1 , wherein the coating layer has a crystal phase or a spinel-like crystal phase, each belonging to the Space Group Fm-3m.
9. The composite cathode active material of claim 1 , wherein the coating layer has a thickness of about 1 nm to about 50 nm.
10. A cathode comprising the composite cathode active material according to claim 1 .
11. A lithium secondary battery comprising the cathode according to claim 10 .
12. A method of preparing a composite cathode active material, the method comprising:
preparing a precursor compound of a lithium transition metal oxide represented by Formula 3;
thermally treating the precursor compound to thereby obtain a core comprising the lithium transition metal oxide;
forming, on a surface of the core, a coating layer comprising a cobalt oxide:
Li x Co 1-y-q-r Ni y M3 q M4 r O 2 <Formula 3>
wherein, in Formula 3, 1.00≤x≤1.04, 0.05≤y≤0.1, 0<q<0.005, 0<r<0.005, 0.001≤q+r≤0.007, and M3 and M4 are different from one another and are each independently selected from magnesium (Mg), and titanium (Ti).
13. The method of claim 12 , wherein the preparing of the precursor compound of the lithium transition metal oxide comprises mechanically mixing a lithium precursor compound, a cobalt precursor compound, a nickel precursor compound, and a precursor compound including at least one element selected from magnesium (Mg) and titanium (Ti) in an atmospheric or oxidizing condition.
14. The method of claim 12 , wherein the thermal treatment comprises a first thermal treatment step and a second thermal treatment step, the first thermal treatment step is followed by the second thermal treatment step, and a thermal treatment temperature in the first thermal treatment step is lower than a thermal treatment temperature in the second thermal treatment step.
15. The method of claim 14 , wherein the first thermal treatment step comprises thermal treatment at a temperature of about 300° C. to about 500° C. under an atmospheric or oxidizing condition for about 3 hours to about 5 hours.
16. The method of claim 14 , wherein the second thermal treatment step comprises thermal treatment at a temperature of about 700° C. to about 1000° C. under an atmospheric or oxidizing condition for about 5 hours to about 12 hours.
17. The method of claim 12 , wherein the forming of the coating layer comprises:
mixing the core comprising the lithium transition metal oxide and a Co precursor compound to thereby prepare a mixture; and
thermally treating the mixture at a temperature of about 700′C to about 950′C in an atmospheric or oxidizing condition for about 3 hours to about 10 hours.