Water-absorbent resin particles and method for producing same
Provided is a method for producing water-absorbent resin particles, which is capable of improving the gel strength for the purpose of achieving a good balance between the absorption under load and the rate of liquid permeation through gel. The present invention is a method for producing water-absorbent resin particles, which is characterized by comprising a step wherein a monomer composition containing a water-soluble vinyl monomer (a1) and/or a vinyl monomer (a2) that turns into a water-soluble vinyl monomer (a1) by means of hydrolysis and a crosslinking agent (b) is polymerized in the presence of at least one organic main group element compound selected from the group consisting of organic iodine compounds, organic tellurium compounds, organic antimony compounds, and organic bismuth compounds.
1. A method for producing water-absorbent resin particles, comprising a step of polymerizing a monomer composition consisting of a water-soluble vinyl monomer (a1) and/or a vinyl monomer (a2) that turns into a water-soluble vinyl monomer (a1) through hydrolysis and up to 5 mol % of an additional vinyl monomer (a3) copolymerizable with the aforementioned vinyl monomers (a1) and (a2) based on the total number of mols of the vinyl monomer (a1) and the vinyl monomer (a2) and a crosslinking agent (b) in the presence of at least one organic main group element compound selected from the group consisting of organic iodine compounds having a tertiary carbon atom to which an iodo group attaches, wherein the monomer composition contains at least one of acrylic acid, methacrylic acid, a salt of acrylic acid and a salt of methacrylic acid as the water-soluble vinyl monomer (a1) in an amount of at least 75 mol % based on the total number of moles of the vinyl monomer (a1) and the vinyl monomer (a2), wherein the method includes a step of surface-crosslinking the crosslinked polymer (A).
2. The method for producing a water-absorbent resin particle according to claim 1 , wherein the organic main group element compound is represented by the following formula (1):
in the formula (1), R 1 and R 2 each independently represent a saturated hydrocarbon group having 1 to 7 carbon atoms, or a monovalent group having 1 to 7 carbon atoms and having at least one non-addition-polymerizable double bond or at least one non-addition-polymerizable triple bond and R 3 represents an n-valent saturated hydrocarbon group having 1 to 7 carbon atoms or an n-valent group having 2 to 12 carbon atoms and having at least one non-addition-polymerizable double bond or at least one non-addition-polymerizable triple bond, provided that at least one of R 1 to R 3 in one molecule is a corresponding group having a non-addition-polymerizable double bond or at least one non-addition-polymerizable triple bond; n is an integer of 1 to 3; when n is 1, R 1 and R 2 may be bonded to each other; X 1 is an iodo group.
3. The method for producing a water-absorbent resin particle according to claim 1 , wherein the weight of organic iodine compounds is 0.0005 to 0.1% by weight relative to the total weight of the water-soluble vinyl monomer (a1) and the vinyl monomer (a2) that turns into a water-soluble vinyl monomer (a1) through hydrolysis.
4. The method for producing a water-absorbent resin particle according to claim 1 , wherein the organic main group element compound is at least one selected from the group consisting of 2-methyl-2-iodopropionitrile, ethyl-2-methyl-2-iodopropinate, 2-methyl-2-iodopropionic acid (salt), ethylene glycol bis(2-methyl-2-iodo-propinate.