Method of producing titanium oxide
Provided is a method of producing a titanium oxide in which titanium tetrachloride is hydrolyzed using a liquid-phase method. This method includes a step of adding an aqueous titanium tetrachloride solution to warm water having a higher temperature than the aqueous titanium rachloride solution, in which in the step, the temperature of the warm water is 30° C. to 95° C. and the aqueous titanium tetrachloride solution is added to the warm water such that an increase rate of titanium atomic concentration in the warm water is 0.25 mmol/L/min to 5.0 mmol/L/min, and a titanium atomic concentration in the warm water after the step is 280 mmol/L or lower.
1. A method of producing a titanium oxide in which titanium tetrachloride is hydrolyzed using a liquid-phase method, the method comprising:
a step of adding an aqueous titanium tetrachloride solution to warm water having a higher temperature than the aqueous titanium tetrachloride solution,
wherein in the step, the temperature of the warm water is 30° C. to 95° C. and the aqueous titanium tetrachloride solution is added to the warm water such that an increase rate of titanium atomic concentration in the warm water is 2.0 mmol/L/min to 5.0 mmol/L/min,
a titanium atomic concentration in the warm water after the step is 280 mmol/L or lower,
the titanium tetrachloride is hydrolyzed in the presence of a water-soluble organic acid having a carboxyl group and/or an inorganic acid, and
the organic acid and/or the inorganic acid is added to the aqueous titanium tetrachloride solution in advance before adding the aqueous titanium tetrachloride solution to the warm water.
2. The method of producing a titanium oxide according to claim 1 ,
wherein the organic acid and/or the inorganic acid is a polyacid.
3. The method of producing a titanium oxide according to claim 1 , further comprising
a dechlorination step of separating a titanium oxide and hydrochloric acid, which are produced in the step of adding the aqueous titanium tetrachloride solution, from each other using at least one selected from the group consisting of an ultrafiltration membrane, a reverse osmosis membrane, an ion exchange resin, and an electrodialytic membrane.
4. The method of producing a titanium oxide according to claim 1 , further comprising
a step of cooling the warm water immediately after the step of adding the aqueous titanium tetrachloride solution to the warm water.