Polybutylene terephthalate resin composition
A polybutylene terephthalate resin composition in which it is possible to effectively suppress discoloration without lowering the heat shock resistance. The polybutylene terephthalate resin composition is part of a molded article having a lightness L* value of 80 or higher as measured using a color difference meter, and includes a polybutylene terephthalate resin having a terminal carboxyl group content of 30 meq/kg or less, a carbodiimide compound, and a phosphite compound; and the phosphite compound content is 0.05-0.15 parts by mass per 100 parts by mass of polybutylene terephthalate resin.
1. A polybutylene terephthalate resin composition for forming a molded article for a housing of a sensor or ECU used for electric control in the automotive field, the molded article having a lightness L* value of 80 or more as measured with a color difference meter, the polybutylene terephthalate resin composition comprising:
a polybutylene terephthalate resin having a terminal-carboxyl group content of 30 meq/kg or less; an aromatic carbodiimide compound; and a phosphite-based compound,
the content of the phosphite-based compound being 0.05 parts by mass or more to 0.12 parts by mass or less per 100 parts by mass of the polybutylene terephthalate resin.
2. The polybutylene terephthalate resin composition according to claim 1 , wherein the content of the aromatic carbodiimide compound is 0.01 parts by mass or more to 5.0 parts by mass or less per 100 parts by mass of the polybutylene terephthalate resin.
3. The polybutylene terephthalate resin composition according to claim 1 or 2 , wherein the molded article has heat shock resistance of 300 cycles or more as measured according to a heat shock resistance test, and has an increase in a hue b* value by 5 or less before and after treatment as measured with a color difference meter before and after cold and heat treatment of 120° C.×1000 hours,
the heat shock resistance test being defined as follows:
a cycle where the molded article is heated at 140° C. for 1 hour and 30 minutes in a cold and heat shock testing machine, and then cooled to −40° C. and maintained for 1 hour and 30 minutes, and then heated to 140° C. again is repeated to determine the number of cycles until a crack occurs in the molded article, thereby evaluating heat shock resistance.
4. The polybutylene terephthalate resin composition according to claim 3 , wherein the molded article has a hue b* value of 10 or less as measured with a color difference meter before and after the cold and heat treatment of 120° C.×1000 hours.