Thermoplastic ABS composition reinforced with natural fibres
The present invention relates to a thermoplastic ABS composition reinforced with natural fibres, which comprises an ABS polymer, natural fibres, a compatibilizing polymer, and processing aids comprising a lubricant and titanium dioxide. It relates also to a moulded article prepared from the thermoplastic composition and to its use in extrusion, injection, compression moulding and 3D printing.
1. Thermoplastic composition comprising:
1) an acrylonitrile-butadiene-styrene (ABS) polymer,
2) natural fibres,
3) a compatibilizing polymer, and
4) processing aids comprising a lubricant and titanium dioxide,
wherein the amount of titanium dioxide is comprised from 1 to 10 wt. %
wherein the compatibilizing polymer is a copolymer of styrene and maleic anhydride or a copolymer of styrene maleic anhydride and N-phenylmaleimide.
2. Thermoplastic composition according to claim 1 , wherein the amount of ABS polymer is comprised from 40 to 90 wt. %.
3. Thermoplastic composition according to claim 1 , wherein the ABS polymer comprises at least one grafted ABS polymer, with a glass transition temperature Tg<0° C.
4. Thermoplastic composition according to claim 3 , additionally comprising at least one rubber-free copolymer.
5. Thermoplastic composition according to claim 3 , wherein the grafted ABS is obtainable by bulk polymerization process containing at least 50 parts of a grafted vinyl aromatic compound and vinyl cyanide compound in a weight ratio of 90:10 to 50:50, in the presence of from 3 to 50 parts of a butadiene polymer.
6. Thermoplastic composition according to claim 3 , wherein the grafted ABS is obtainable by emulsion polymerization process containing at least 25 parts of a grafted vinyl aromatic compound and vinyl cyanide compound in a weight ratio of 90:10 to 50:50, in the presence of not more than 75 parts a butadiene polymer.
7. Thermoplastic composition according to claim 6 , wherein the grafted ABS is obtainable by emulsion polymerization process containing at least 40 parts of a grafted vinyl aromatic compound and vinyl cyanide compound in a weight ratio of 90:10 to 50:50, in the presence of at least 50 parts of a butadiene polymer.
8. Thermoplastic composition according to claim 4 , wherein the rubber-free copolymer is comprised of styrene and acrylonitrile in a weight ratio of from 90:10 to 50:50.
9. Thermoplastic composition according to claim 1 , wherein the natural fibres are cellulose based natural fibres or wood fibres.
10. Thermoplastic composition according to claim 1 , wherein the lubricant is selected from the group consisting of stearates, paraffin oils, polyethylene waxes, lauric acid, palmitic acid, stearic acid, stearic acid amides, ethylenediamine, glycerol, and mixtures thereof.
11. Thermoplastic composition according to claim 1 , further comprising antioxidants, antistatic agents, mould releasing agents, colorants, pigments, mineral fillers, visible light and UV stabilizers, and mixtures thereof.
12. A moulded article prepared from the thermoplastic composition of claim 1 .
13. A method of manufacturing an article comprising using the thermoplastic composition of claim 1 in extrusion, injection, compression moulding or 3D printing.