Reflective coating
Compositions containing diamond particles for producing reflective coatings and methods of wet and dry application of diamond particles to substrates to produce reflective coatings. The coatings have a desirable appearance, are robust and easy to apply.
1. A liquid composition comprising:
visible, reflective diamond particles, wherein substantially all of the diamond particles have a largest dimension in the range of 35-175 μm; and
a binder which is transparent when the liquid composition dries to form a solid coating,
wherein the liquid composition is used for producing the solid coating, wherein said diamond particles are visible and reflective in the solid coating.
2. The liquid composition according to claim 1 , wherein substantially all of the diamond particles have a largest dimension in the range of 35-100 μm.
3. The liquid composition according to claim 1 , wherein substantially all of the diamond particles have a largest dimension in the range of 50-175 μm.
4. The liquid composition according to claim 1 , wherein the particle size ranges are obtained by sieving.
5. The liquid composition according to claim 1 , wherein the diamond particles are natural diamond particles.
6. The liquid composition according to claim 1 , wherein the ratio between the mass of the diamond particles and the mass of the binder is between 5:100 and 15:100.
7. The liquid composition according to claim 1 , wherein the binder is transparent.
8. A method of producing a reflective coating, comprising the steps of:
(i) applying liquid composition of claim 1 to a substrate; and
(ii) causing or allowing the composition to dry to form an initial reflective coating.
9. The method according claim 8 , wherein the method further comprises the step of:
(iii) applying a further said liquid composition over the initial reflective coating, wherein substantially all of the diamond particles in the further composition applied in step (iii) have a largest dimension which is smaller than the largest dimension of substantially all of the diamond particles in the initial reflective coating.
10. The method according to claim 8 , wherein the method further comprises the step of:
(iii) applying a further said liquid composition over the initial reflective coating, wherein substantially all of the diamond particles in the further composition applied in step (iii) have a largest dimension which is larger than the largest dimension of substantially all of the diamond particles in the initial reflective coating.
11. The method according to claim 8 , wherein the method further comprises the step of applying a protective layer over the initial reflective coating.
12. The method according to claim 11 , wherein the substrate is transparent and wherein the protective layer is opaque.
13. The method according to claim 11 , wherein the substrate is opaque, and wherein the protective layer is transparent.
14. The method according to claim 8 , wherein the substrate is glass.
15. The method according to claim 8 , wherein the diamond particles have a morphology consistent with having been obtained by crushing larger particles.
16. The method according to claim 8 , wherein the diamond particles are natural diamond particles.
17. The method according to claim 8 , wherein the composition is applied so that 20-40 g of diamond particles are present in the reflective coating per square meter of substrate.
18. The method according to claim 8 , wherein the composition is applied so that 25-30 g of diamond particles are present in the reflective coating per square meter of substrate.
19. An article comprising a dried liquid composition according to claim 1 .
20. The article according to claim 19 , wherein the article is an item of furniture, or a vehicle, or a wearable item, or an architectural feature.
21. The liquid composition according to claim 1 , wherein substantially all of the diamond particles have a largest dimension in the range of 35-55 μm.
22. The liquid composition according to claim 1 , wherein substantially all of the diamond particles have a largest dimension in the range of 37-44 μm.
23. The liquid composition according to claim 1 , wherein substantially all of the diamond particles have a largest dimension in the range of 44-53 μm.
24. The liquid composition according to claim 1 , wherein substantially all of the diamond particles have a largest dimension in the range of 100-175 μm.
25. The liquid composition according to claim 1 , wherein substantially all of the diamond particles have a largest dimension in the range of 145-175 μm.
26. The liquid composition according to claim 1 , wherein the diamond particles are natural diamond particles and have a morphology consistent with having been obtained by crushing larger particles.
27. The liquid composition according to claim 1 , wherein the ratio between the mass of the diamond particles and the mass of the binder is between 7:100 and 10:100.
28. The liquid composition according to claim 1 , wherein the binder is clear coat.