Color development of carbon black in expanded polystyrene
When long chain primary alcohols are into expanded polystyrene (EPS) containing an additive such as carbon black or graphite to give gray EPS, the long chain primary alcohols act as color enhancing agents and generate a darker color as compared with an otherwise identical gray EPS absent the additive.
1. A method for preparing gray expanded polystyrene (EPS), the method comprising:
polymerizing styrene monomer and a polymerization initiator by suspension polymerization;
introducing into the suspension polymerization an additive selected from the group consisting of carbon black, graphite, and combinations thereof;
before, during or after introducing the additive, introducing into the suspension polymerization at least one color enhancing agent selected from the group consisting of long chain primary alcohols, long chain primary alcohols modified with a polar group, and combinations thereof, where the long chain primary alcohols have a weight average molecular weight of from about 250 amu to about 2000 amu; and
continuing to polymerize the styrene monomer to polystyrene by suspension polymerization to produce gray EPS.
2. The method of claim 1 where the long chain primary alcohols modified with a polar group comprise long chain primary alcohols modified with 1 to 7 ethoxylate groups.
3. The method of claim 1 where the amount of at least one color enhancing agent ranges from about 500 to about 3000 ppm based on the styrene monomer present.
4. The method of claim 1 where the gray EPS is darker than an identical gray EPS absent the color enhancing agent.
5. The method of claim 1 where the gray EPS:
has a weight average molecular weight between about 50,000 and about 1,000,000 amu;
has a bead size between about 500 and about 1500 microns;
has a bead distribution where from about 10 to about 90 weight % of the beads are in the range of about 850 to about 1170 microns; and
has a cell size between about 4 and about 20 cells per millimeter.
6. The method of claim 1 where the gray EPS has a density from about 5 to about 35 g/l.
7. The method of claim 1 where the amount of additive ranges from about 0.1 to about 10 wt %, based on the produced gray EPS.
8. A method for preparing gray expanded polystyrene (EPS), the method comprising:
polymerizing styrene monomer and a polymerization initiator by suspension polymerization;
introducing into the suspension polymerization an additive selected from the group consisting of carbon black, graphite, and combinations thereof, where the amount of additive ranges from about 0.1 to about 10 wt %, based on the produced gray EPS; and
before, during or after introducing the additive, introducing into the suspension polymerization at least one color enhancing agent selected from the group consisting of long chain primary alcohols, long chain primary alcohols modified with a polar group, and combinations thereof, where the long chain primary alcohols have a weight average molecular weight of from about 250 amu to about 2000 amu, where the amount of additive ranges from about 500 to about 3000 ppm based on the styrene monomer present; and
continuing to polymerize the styrene monomer to polystyrene by suspension polymerization to produce gray EPS.
9. The method of claim 8 where the long chain primary alcohols modified with a polar group comprise long chain primary alcohols modified with 1 to 7 ethoxylate groups.
10. The method of claim 8 where the gray EPS is darker than an identical gray EPS absent the color enhancing agent.
11. The method of claim 8 where the gray EPS:
has a weight average molecular weight between about 50,000 and about 1,000,000 amu;
has a bead size between about 500 and about 1500 microns;
has a bead distribution where from about 10 to about 90 weight % of the beads are in the range of about 850 to about 1170 microns; and
has a cell size between about 4 and about 20 cells per millimeter.
12. The method of claim 8 where the gray EPS has a density from about 5 to about 35 g/l.
13. A method for preparing gray expanded polystyrene (EPS), the method comprising:
polymerizing styrene monomer and a polymerization initiator by suspension polymerization;
introducing into the suspension polymerization an additive selected from the group consisting of carbon black, graphite, and combinations thereof; and
before, during or after introducing the additive, introducing into the suspension polymerization at least one color enhancing agent selected from the group consisting of long chain primary alcohols, long chain primary alcohols modified with a polar group, and combinations thereof, where the long chain primary alcohols have a weight average molecular weight of from about 250 amu to about 2000 amu; and
continuing to polymerize the styrene monomer to polystyrene by suspension polymerization to produce gray EPS, where the gray EPS is darker than an identical gray EPS absent the additive, and has a density from about 5 to about 35 g/l.
14. The method of claim 13 where the long chain primary alcohols modified with a polar group comprise long chain primary alcohols modified with 1 to 7 ethoxylate groups.
15. The method of claim 13 where the amount of at least one color enhancing agent ranges from about 500 to about 3000 ppm based on the styrene monomer present.
16. The method of claim 13 where the gray EPS:
has a weight average molecular weight between about 50,000 and about 1,000,000 amu;
has a bead size between about 500 and about 1500 microns;
has a bead distribution where from about 10 to about 90 weight % of the beads are in the range of about 850 to about 1170 microns; and
has a cell size between about 4 and about 20 cells per millimeter.
17. The method of claim 13 where the amount of additive ranges from about 0.1 to about 10 wt %, based on the produced gray EPS.