Methods for self-aligned patterning
Processing methods comprising depositing a film on a substrate surface and in a surface feature with chemical planarization to remove the film from the substrate surface, leaving the film in the feature. A pillar is grown from the film so that the pillar grows orthogonally to the substrate surface.
1. A processing method comprising:
providing a substrate with a substrate surface having at least one feature extending into the substrate from the substrate surface, the feature having a bottom and sidewalls;
depositing a first film comprising a metal on the substrate surface so that the first film covers the substrate surface and fills the feature;
chemically planarizing the substrate surface by sequentially oxidizing a top of the first film to form an oxidized first film on top of the first film and etching the oxidized first film to remove the oxidized first film, the sequential oxidizing and etching repeated to remove the first film from the substrate surface leaving the first film in the feature; and
expanding the first film to grow a first pillar in the feature that extends from the feature orthogonally to the substrate surface.
2. The method of claim 1 , wherein the metal comprises tungsten.
3. The method of claim 1 , wherein depositing the first film and chemically planarizing the substrate surface occurs in the same processing chamber.
4. The method of claim 1 , wherein expanding the first film to grow the first pillar comprises one or more of oxidizing or nitriding the first film.
5. The method of claim 4 , wherein the first pillar is grown by exposure to one or more of O 2 , O 3 , H 2 O, H 2 O 2 , H 2 O 4 or N 2 O.
6. The method of claim 1 , wherein removing the first film to expose the substrate surface comprises substantially no mechanical planarization.
7. The method of claim 1 , wherein etching the oxidized first film comprises exposing the first film to a metal halide compound.
8. The method of claim 7 , wherein the metal halide compound and the first film have the same metal.
9. The method of claim 1 , wherein depositing the first film comprises an atomic layer deposition process.
10. The method of claim 9 , wherein depositing the first film comprises sequential exposure to a metal halide precursor and a reactant to deposit a metal film.
11. The method of claim 10 , wherein chemically planarizing the first film comprises exposure of the oxidized first film to the same metal halide precursor.
12. The method of claim 11 , wherein the metal halide precursor comprises a tungsten halide.
13. The method of claim 12 , wherein the tungsten halide comprises one or more of WCl 5 or WCl 6 .
14. A processing method comprising:
providing a substrate with a substrate surface having at least one feature extending into the substrate from the substrate surface, the feature having a bottom and sidewalls;
depositing a first film comprising a metal on the substrate surface so that the first film covers the substrate surface and fills the feature;
chemically planarizing the substrate surface by sequentially oxidizing a top of the first film to form an oxidized first film on top of the first film and etching the oxidized first film to remove the oxidized first film, the sequential oxidizing and etching repeated to remove the first film from the substrate surface leaving the first film in the feature; and
expanding the first film to grow a first pillar in the feature that extends from the feature orthogonally to the substrate surface.
15. The method of claim 14 , wherein depositing the first film and chemically planarizing the substrate surface occurs in the same processing chamber.
16. The method of claim 14 , wherein expanding the first film to grow the first pillar comprises one or more of oxidizing or nitriding the first film.
17. The method of claim 14 , wherein the metal comprises tungsten.
18. The method of claim 17 , wherein depositing the first film comprises sequential exposure of the substrate surface to a metal halide precursor and a reactant to deposit a metal film and chemically planarizing the first film comprises exposure of the oxidized first film to the same metal halide precursor.
19. A processing method comprising:
providing a substrate with a substrate surface having at least one feature extending into the substrate from the substrate surface, the feature having a bottom and sidewalls;
depositing a first film on the substrate surface by sequential exposure to a metal precursor and a reactant to form a first film that covers the substrate surface and fills the feature, the first film comprising tungsten metal and the metal precursor comprising a tungsten halide;
chemically planarizing the substrate surface by sequentially oxidizing a top of the first film to form an oxidized first film on top of the first film and etching the oxidized first film by exposure to the same tungsten halide compound as the metal precursor to remove the oxidized first film, the sequential oxidizing and etching repeated to remove the first film from the substrate surface leaving the first film in the feature; and
expanding the first film by one or more of oxidizing or nitriding the first film to grow a first pillar in the feature that extends from the feature orthogonally to the substrate surface,
wherein depositing the first film and chemically planarizing the substrate surface occurs in the same processing chamber.