One step synthesis of ultrahigh molecular weight block copolymers
Single-step synthesis processes for production of ultrahigh molecular weight block copolymers are described. The ultrahigh molecular weight copolymers can have a molecular weight of about 10 6 or greater and can be formed within a few hours in a surfactant-free environment. The formation process is controlled by initiator-starvation conditions in a sequential polymerization of monomers exhibiting different solubility in the solvent.
1. A method for forming ultrahigh molecular weight amphiphilic block copolymers comprising
combining a hydrophilic monomer and a hydrophobic monomer in an aqueous solvent, the hydrophilic monomer exhibiting greater solubility in the aqueous solvent as compared to the hydrophobic monomer, the hydrophobic monomer aggregating in the aqueous solvent to form dispersed droplets upon addition of the hydrophobic monomer to the aqueous solvent, the concentration of the hydrophilic monomer in the aqueous solvent being greater than the concentration of the hydrophobic monomer in the aqueous solvent; and
adding a polymerization initiator to the aqueous solvent at a rate of about 0.1 milligrams initiator per minute or slower, wherein the initiator is soluble in the aqueous solvent at the reaction conditions, upon which ultrahigh molecular weight amphiphilic block copolymers having a number average molecular weight of about 500,000 or greater forming according to a heterogeneous radical polymerization reaction.
2. The method of claim 1 , wherein no surfactants are added to the solvent.
3. The method of claim 1 , wherein the ultrahigh molecular weight block copolymers are formed over a period of about 6 hours or less.
4. The method of claim 1 , wherein the ultrahigh molecular weight block copolymers are in the form of core/shell nanoparticles.
5. The method of claim 4 , wherein the core/shell nanoparticles form inverse polymeric micelles in response to a stimulation.
6. The method of claim 1 , wherein the ultrahigh molecular weight block copolymers are in the form of nanowires.
7. The method of claim 1 , wherein the aqueous solvent is water.
8. The method of claim 1 , wherein the hydrophobic monomer has a solubility in the aqueous solvent of about 20 grams per liter or less.
9. The method of claim 1 , wherein the reactivity of the hydrophilic monomer to itself is higher than the reactivity of the hydrophilic monomer to the hydrophobic monomer.
10. The method of claim 1 , wherein the hydrophilic monomer comprises a group capable of protonation in the aqueous solvent.
11. The method of claim 10 , wherein the group is a tertiary amine group.
12. The method of claim 1 , wherein the hydrophilic monomer or the hydrophobic monomer comprises a halogen.
13. The method of claim 12 , wherein the hydrophilic monomer or the hydrophobic monomer comprises a fluorine.
14. The method of claim 1 , wherein the ratio of the molar concentration of the hydrophilic monomer to that of the hydrophobic monomer upon combination of the two with the solvent is about 2:1 or higher.
15. The method of claim 1 , wherein the ultrahigh molecular weight block copolymer is a diblock copolymer.
16. The method of claim 1 , wherein the ultrahigh molecular weight block copolymer is a triblock copolymer.