Method of manufacturing metal-clad laminate and uses of the same
A method of manufacturing a metal-clad laminate and uses of the same are provided. The method comprises the following steps: (a) impregnating a reinforcement material with a first fluoropolymer solution, and drying the impregnated reinforcement material under a first temperature to obtain a first prepreg; (b) impregnating the first prepreg with a second fluoropolymer solution, and drying the impregnated first prepreg under a second temperature to obtain a second prepreg; and (c) laminating the second prepreg and a metal-clad to obtain a metal-clad laminate, wherein the first fluoropolymer solution has a first fluoropolymer, the second fluoropolymer solution has a second fluoropolymer, and the first fluoropolymer and the second fluoropolymer are different.
1. A manufacturing method of a metal-clad laminate, comprising the following steps:
(a) impregnating a reinforcement material with a first fluoropolymer solution, and drying the impregnated reinforcement material at a first temperature to obtain a first prepreg;
(b) impregnating the first prepreg with a second fluoropolymer solution, and drying the impregnated first prepreg at a second temperature to obtain a second prepreg; and
(c) laminating the second prepreg and a metal foil to obtain a metal-clad laminate,
wherein the first fluoropolymer solution has a first fluoropolymer, the second fluoropolymer solution has a second fluoropolymer, and the first fluoropolymer and the second fluoropolymer are different,
wherein the method does not use an epoxy resin and does not use an adhesive film to attach the metal foil, and
wherein the first prepreg and the second prepreg are prepared at a process temperature not higher than 300° C.
2. The manufacturing method of claim 1 , wherein in step (a), the impregnating and drying are repeated in the same order at least one more time.
3. The manufacturing method of claim 1 , wherein in step (b), the impregnating and drying are repeated in the same order at least one more time.
4. The manufacturing method of claim 1 , wherein the metal foil is a low profile metal foil.
5. The manufacturing method of claim 1 , wherein the melting temperature of the second fluoropolymer is lower than the melting temperature of the first fluoropolymer.
6. The manufacturing method of claim 5 , wherein in step (a), the impregnating and drying are repeated in the same order at least one more time.
7. The manufacturing method of claim 5 , wherein in step (b), the impregnating and drying are repeated in the same order at least one more time.
8. The manufacturing method of claim 5 , wherein the metal foil is a low profile metal foil.
9. The manufacturing method of claim 1 , wherein the first fluoropolymer is polytetrafluoroethylene (PTFE).
10. The manufacturing method of claim 9 , wherein in step (a), the impregnating and drying are repeated in the same order at least one more time.
11. The manufacturing method of claim 9 , wherein in step (b), the impregnating and drying are repeated in the same order at least one more time.
12. The manufacturing method of claim 9 , wherein the metal foil is a low profile metal foil.
13. The manufacturing method of claim 1 , wherein the second fluoropolymer is selected from the group consisting of fluorinated ethylene propylene (FEP), polyfluoroalkoxy (PFA), and combinations thereof.
14. The manufacturing method of claim 13 , wherein in step (a), the impregnating and drying are repeated in the same order at least one more time.
15. The manufacturing method of claim 13 , wherein in step (b), the impregnating and drying are repeated in the same order at least one more time.
16. The manufacturing method of claim 13 , wherein the metal foil is a low profile metal foil.