Heat transfer tube and method for producing same
A heat transfer tube includes: a tube body made of an extruded material of an aluminum alloy having a composition including: 0.3 mass % or more and less than 0.8 mass % of Mn; more than 0.1 mass % and less than 0.32 mass % of Si; 0.3 mass % or less of Fe; 0.06 mass % or more and 0.3 mass % or less of Ti; and Al balance including inevitable impurities, a ratio of a Mn content to a Si content, Mn %/Si %, exceeding 2.5; and a Zn-containing layer provided to an outer surface of the tube body.
1. An extruded heat transfer tube with internal passages, the heat transfer tube comprising:
a tube body made of an extruded material of an aluminum alloy having a composition including: 0.3 mass % or more and less than 0.8 mass % of Mn; more than 0.1 mass % and less than 0.32 mass % of Si; 0.3 mass % or less of Fe; 0.06 mass % or more and 0.3 mass % or less of Ti; and Al balance including inevitable impurities, a ratio of a Mn content to a Si content, Mn %/Si %, exceeding 2.5; and
a Zn-containing layer provided to an outer surface of the tube body, wherein the internal passages are divided by a wall with a thickness of 1.5 mm or less, the heat transfer tube has an extrusion weld part by being formed by extruding works,
selective corrosion at the extrusion weld part is suppressed,
wherein 2200/mm 2 or less of intermetallic compound precipitates whose size is 1.0 μm or more in a circle equivalent diameter are precipitated in the heat transfer tube after a brazing heat treatment or a Zn diffusing treatment of the heat transfer tube,
the aluminum alloy constituting the tube body is an alloy subjected to a homogenization treatment in which an ingot of the aluminum alloy after casting is kept at 450-650° C. for 2-24 hours,
a heating rate from a room temperature to 450° C. is 50-180° C./h; a heating rate from 450° C. to a temperature of the homogenization treatment is 10-80° C./h; and a cooling rate from the temperature of the homogenization treatment to 200° C. is 50-400° C./h, in the homogenization treatment, and
a brazing heat treatment or a Zn diffusing treatment is performed on the heat transfer tube at 610° C. or lower.
2. The heat transfer tube according to claim 1 , wherein the aluminum alloy further includes: 0.05 mass % or less of Cu; less than 0.05 mass % of Mg; and less than 0.03 mass % of Cr.
3. The heat transfer tube according to claim 1 , wherein the aluminum alloy constituting the tube body is an alloy subjected to a homogenization treatment in which an ingot of the aluminum alloy after casting is kept at 450-650° C. for 2-24 hours.
4. The heat transfer tube according claim 1 , wherein a brazing heat treatment or a Zn diffusing treatment is performed on the heat transfer tube at 610° C. or lower.
5. The heat transfer tube according to claim 1 , wherein a refrigerant that is flowing inside the heat transfer tube is fluorocarbon.