Ultraviolet curable primer for radio-wave transmission cover of vehicle
An ultraviolet curable primer for a radio-wave transmission cover of a vehicle may include about 20 wt % to about 30 wt % of urethane acrylate oligomer, about 35 wt % to about 60 wt % of monomer, about 1 wt % to about 5 wt % of photopolymerization initiator, about 0.1 wt % to about 1.0 wt % of wetting additive, and about 10 wt % to about 30 wt % of solvent, wherein the urethane acrylate oligomer comprises about 7.5 wt % to about 12.5 wt % of two-function urethane acrylate oligomer based on the total weight of the ultraviolet curable primer, and about 12.5 wt % to about 17.5 wt % of six-function urethane acrylate oligomer based on the total weight of the ultraviolet curable primer, and wherein the ultraviolet curable primer is applied to a radio-wave transmission cover comprising a multilayered oxide optical film.
1. An ultraviolet curable primer for a radio-wave transmission cover of a vehicle comprising:
about 20 wt % to about 30 wt % of urethane acrylate oligomer, about 35 wt % to about 60 wt % of monomer, about 1 wt % to about 5 wt % of photopolymerization initiator, about 0.1 wt % to about 1.0 wt % of wetting additive, and about 10 wt % to about 30 wt % of solvent,
wherein the urethane acrylate oligomer comprises about 7.5 wt % to about 12.5 wt % of two-function urethane acrylate oligomer based on the total weight of the ultraviolet curable primer, and about 12.5 wt % to about 17.5 wt % of six-function urethane acrylate oligomer based on the total weight of the ultraviolet curable primer, and
wherein the ultraviolet curable primer is applied to a radio-wave transmission cover comprising a multilayered oxide optical film.
2. The ultraviolet curable primer according to claim 1 , wherein the monomer comprises about 10 wt % to about 20 wt % of pentaerythritol tetraacrylate (PETA), 20 to 30 wt % of trimethyol propane triacrylate (TMPTA), and about 5 wt % to about 10 wt % of hexandiol diacrylate (HDDA) based on the total weight of the ultraviolet curable primer.
3. The ultraviolet curable primer according to claim 1 , wherein the urethane acrylate oligomer is provided by mixing the two-function urethane acrylate oligomer and the six-function urethane acrylate oligomer at a weight ratio of 1:1 to 2.5.
4. The ultraviolet curable primer according to claim 1 , wherein the urethane acrylate oligomer does not comprise a four-function urethane acrylate oligomer.
5. The ultraviolet curable primer according to claim 1 , wherein the urethane acrylate oligomer has a solid content of about 70 wt % to about 80 wt %.
6. The ultraviolet curable primer according to claim 1 , wherein a crack does not occur in the ultraviolet curable primer after elapse of about 10 minutes to about 20 minutes at a temperature of about 220° C. to about 240° C. after the ultraviolet curable primer is dried.
7. The ultraviolet curable primer according to claim 1 , wherein the ultraviolet curable primer has a distinctness of 65 or more after it is dried, and a haze defect does not occur in a film of paint.
8. The ultraviolet curable primer according to claim 2 , wherein the urethane acrylate oligomer is provided by mixing the two-function urethane acrylate oligomer and the six-function urethane acrylate oligomer at a weight ratio of 1:1 to 2.5.
9. The ultraviolet curable primer according to claim 2 , wherein the urethane acrylate oligomer does not comprise a four-function urethane acrylate oligomer.
10. The ultraviolet curable primer according to claim 2 , wherein the urethane acrylate oligomer has a solid content of about 70 wt % to about 80 wt %.
11. The ultraviolet curable primer according to claim 2 , wherein a crack does not occur in the ultraviolet curable primer after elapse of about 10 minutes to about 20 minutes at a temperature of about 220° C. to about 240° C. after the ultraviolet curable primer is dried.
12. The ultraviolet curable primer according to claim 2 , wherein the ultraviolet curable primer has a distinctness of 65 or more after it is dried, and a haze defect does not occur in a film of paint.