Zirconium oxide based sputtering target
The present invention relates to a sputtering target, which comprises a zirconium oxide as a sputtering material, wherein the zirconium oxide has an oxygen deficiency, compared to the oxygen content of its fully oxidized form, of at least 0.40 wt %, has a total amount of metal elements other than zirconium of less than 3.0 wt %, based on the total amounts of metal elements including zirconium, and has an X-ray powder diffraction pattern having a peak P1 at 28.2°+/−0.2° 2-theta, a peak P2 at 31.4°+/−0.2° 2-theta, and a peak P3 at 30.2°+/−0.2° 2-theta.
1. A sputtering target, which consists essentially of a zirconium oxide as a sputtering material, wherein the zirconium oxide
has an oxygen deficiency, compared to the oxygen content of its fully oxidized form, of at least 0.40 wt %,
consists of zirconium, oxygen, and a total amount of metal elements other than zirconium of less than 3.0 wt %, based on the total amounts of metal elements including zirconium, the remainder being unavoidable impurities, and
has an X-ray powder diffraction pattern having a peak P1 at 28.2°+/−0.2° 2-theta, a peak P2 at 31.4°+/−0.2° 2-theta, and a peak P3 at 30.2°+/−0.2° 2-theta; and
wherein the zirconium oxide is a mixture of two or more crystalline zirconium oxide phases and one of the two or more crystalline zirconium oxide phases is monoclinic; wherein the sputtering material is sprayed onto a backing tube.
2. The sputtering target according to claim 1 , wherein the peak P1 is the peak of highest intensity, and the peak P2 is the peak of second-highest intensity in the X-ray diffraction pattern of the zirconium oxide, and the intensity ratio P3/P2 is at least 0.06.
3. The sputtering target according claim 2 , wherein the X-ray diffraction pattern of the zirconium oxide shows further peaks at 24.2°+/−0.2° 2-theta, 34.3°+/−0.2° 2-theta, and 50.2°+/−0.2° 2-theta.
4. The sputtering target according to claim 3 , wherein the zirconium oxide has an average crystallite size, determined by applying the Scherrer equation to the most intensive diffraction peak, of less than 63 nm.
5. The sputtering target according to claim 2 , wherein the zirconium oxide does not comprise pores which have a diameter of more than 70 μm.
6. The sputtering target according to claim 2 , wherein the zirconium oxide has a relative density of at least 85%.
7. The sputtering target according to claim 1 , wherein the zirconium oxide has an average crystallite size, determined by applying the Scherrer equation to the most intensive diffraction peak, of less than 63 nm.
8. The sputtering target according claim 1 , wherein the X-ray diffraction pattern of the zirconium oxide shows further peaks at 24.2°+/−0.2° 2-theta, 34.3°+/−0.2° 2-theta, and 50.2°+/−0.2° 2-theta.
9. The sputtering target according to claim 1 , wherein the zirconium oxide does not comprise pores which have a diameter of more than 70 μm.
10. The sputtering target according to claim 1 , wherein the zirconium oxide has a relative density of at least 85%.
11. The sputtering target according to claim 1 , wherein the zirconium oxide represents at least 75 wt % of the sputtering material.
12. Use of the sputtering target according claim 1 for DC sputtering.
13. The sputtering target of claim 1 , wherein the zirconium oxide has a specific resistivity of 10 Ωcm or less.