Method for analytically determining laser power for laser sintering

1. A method of analytically determining a laser power for configuring a laser in a selective laser sintering process, comprising:

choosing a batch of polymer powder material for building a plurality of test rods;

selecting a range of laser power for building the plurality of test rods;

determining a plurality of power increments within the selected range to define a plurality of different laser power settings;

programming a selective laser sintering machine to build at least one test rod of said plurality of test rods at each laser power setting;

constructing the plurality of test rods from the batch of powder material based on said programming;

inspecting each test rod for voids in a surface of the test rod, the voids having a width of a least 0.005″;

identifying the laser power setting used to construct a respective test rod without formation of voids in the surface as an optimal laser power; and

configuring the selective laser sintering machine with the optimal laser power when conducting a laser sintering process using the chosen batch of powder material.

2. The method of claim 1 , further comprising:

measuring a tensile strength of each test rod to obtain tensile strength results;

and comparing the tensile strength results.

3. The method of claim 2 , wherein the step of measuring the tensile strength of each test rod comprises testing each test rod according to ASTM D638 test process.

4. The method of claim 2 , wherein the step of measuring the tensile strength of each test rod comprises measuring the tensile strength of each test rod in a z-axis and comparing the tensile strength results to determine which test rod of said plurality of test rods provides a higher break point in the z-axis.

5. The method of claim 1 , further comprising inspecting a fracture point of each test rod, the fracture point formed during an ASTM D638 test process.

6. The method of claim 5 , wherein the step of inspecting each test rod further comprises inspecting a porosity of each test rod.

7. The method of claim 1 , wherein the optimal laser power is at least one watt below a lowest laser power setting associated with the formation of voids.

8. The method of claim 1 , wherein the step of inspecting each test rod for voids comprises inspecting an x-axis of each test rod for presence of voids.

9. The method of claim 2 , wherein the step of identifying the optimal laser power comprises selecting a laser power setting based on the absence of voids in the respective test rod and on the tensile strength of the respective rod, wherein the optimal laser power provides the highest strength in z-axis with no formation of voids.

10. The method of claim 2 , wherein the step of measuring the tensile strength of each test rod comprises measuring at least one of the following for each test rod: Young's modulus, elongation to break, elongation at yield, nominal strain at break, secant modulus of elasticity, or Poisson's Ratio.

11. The method of claim 1 , wherein the chosen batch of powder material comprises PEKK polymer.

12. The method of claim 11 , wherein the chosen batch of powder material comprises recycled PEKK polymer.

13. The method of claim 1 , wherein the step of selecting a range of laser power comprises selecting a range between 1 W and 20 W.

14. The method of claim 13 , wherein the step of selecting a range of laser power comprises selecting a range between 5 W and 15 W.

15. A method of analytically determining a low laser power for configuring a laser in a laser sintering process, comprising:

choosing a batch of polymer powder material for building a plurality of test rods having substantially identical shapes;

selecting a range of laser power between 5 W and 15 W for building the plurality of test rods;

determining a plurality of power increments within the selected range to define a plurality of different laser power settings;

programming a selective laser sintering machine to build at least one test rod of said plurality of test rods at each laser power setting;

constructing the plurality of test rods from the batch of powder material based on said programming, wherein the test rods are oriented along a z-axis in a build chamber of the selective laser sintering machine;

inspecting each test rod for voids in a surface of the test rod, the voids having a width of a least 0.005″;

measuring a tensile strength of each test rod to obtain tensile strength results;

comparing the tensile strength results to determine the test rod with the highest tensile strength;

identifying the laser power setting used to construct a respective test rod having no formation of voids and high strength in the z-axis as an optimal laser power; and

configuring the selective laser sintering machine with the optimal laser power when conducting a laser sintering process using the chosen batch of powder material.

16. The method of claim 15 , wherein the optimal laser power is at least one watt below a lowest laser power setting associated with the formation of voids.

17. The method of claim 15 , wherein the step of programming comprises programming the selective laser sintering machine to build at least five test rods of said plurality of test rods at each laser power setting.

18. The method of claim 15 , wherein said plurality of different laser power settings comprises at least eight different last power settings.

19. The method of claim 15 , wherein the step of programming comprises programming the selective laser sintering machine to build said plurality of test rods in one single build run.