Transparent oriented polypropylene film with high moisture vapor and oxygen barrier properties
Described are transparent oriented polypropylene films with improved barrier properties and methods of making these films. The films and methods include a core layer comprising polypropylene, hydrocarbon resin, and polyethylene wax to improve moisture vapor barrier properties, an optional barrier layer comprising polar polymers to improve oxygen barrier properties, and optional skin layers to improve heat sealing, winding, printing, and/or adhesion.
1. A method of making a film comprising:
coextruding a core layer comprising high crystalline polypropylene, hydrocarbon resin, and 0.5 wt. % polyethylene wax with a skin layer comprising polyolefin; and
adding a barrier layer comprising crosslinked polar polymers on a surface of the core layer opposite the skin layer.
2. The method of claim 1 , wherein the barrier layer is coextruded on the surface of the core layer opposite the skin layer.
3. The method of claim 1 , wherein the barrier layer is coated on the surface of the core layer opposite the skin layer.
4. The method of claim 3 , wherein the film is oriented in the machine direction prior to coating of the barrier layer.
5. The method of claim 4 , wherein the film is oriented in the transverse direction after coating the film with the barrier layer.
6. The method of claim 1 , further comprising coextruding a tie-layer comprising polyolefin on a surface of the core layer opposite the skin layer.
7. The method of claim 6 , wherein the barrier layer is inline or offline coated on the surface of the tie-layer opposite the core layer.
8. The method of claim 6 , wherein the barrier layer is coextruded on the surface of the tie-layer opposite the core layer.
9. The method of claim 1 , further comprising heat aging the film.
10. The method of claim 9 , wherein the aging temperature is lower than a Tg of the hydrocarbon resin and a melting temperature of the polyethylene wax.
11. The method of claim 9 , wherein the aging temperature is from 40-70° C. and the aging time is from 12 to 48 hours.