High performance plastic magnetic materials and preparation method thereof
The invention discloses a high performance plastic magnetic material, comprising a low surface energy layer, a magnetic layer and a printable layer, wherein the magnetic layer and the printable layer are arranged successively on a first side of the low surface energy layer; the low surface energy layer is an organic silicon pressure sensitive adhesive layer. The invention further discloses a preparation method, comprising the following steps: pretreating a magnetic powder with a coupling agent; mixing the pretreated magnetic powder with matrix components and auxiliaries to gain a mixture; extrusion compositing the gained mixture with a printable layer to gain composite paper having the printable layer and a magnetic layer; and applying a low surface energy layer on a side of the magnetic layer, opposite the printable layer. As no UV layer and no adhesive residue, the material of the invention is environmentally friendly and highly reliable.
1. A plastic magnetic material, comprising an organic silicon pressure sensitive adhesive layer, a magnetic layer and a printable layer, wherein the magnetic layer and the printable layer are arranged successively on a first side of the organic silicon pressure sensitive adhesive layer;
wherein the organic silicon pressure sensitive adhesive layer is prepared from the following raw materials: 100 parts of vinyl-terminated polysiloxane, 100-150 parts of solvent, 1-5 parts of crosslinking agent, 1-5 parts of accelerator, and 1-5 parts of catalyst; and
wherein the magnetic layer comprises the following components:
50% wt-90% wt magnetic powder, 7% wt-50% wt matrix component and 0-3% wt auxiliaries;
wherein the vinyl-terminated polysiloxane is selected from a group consisting of vinyl-terminated dimethyl siloxane, vinyl-terminated dimethyl polysiloxane, vinyl-terminated poly (dimethyl siloxane) and combinations thereof, and the vinyl-terminated polysiloxane has a viscosity of 8,000-30,000 mPa*s at 25° C.;
wherein the crosslinking agent is hydrosilicone oil; the catalyst is platinum compounds and/or platinum complexes; and the accelerator is a coupling agent;
wherein the magnetic powder is at least one selected from the group consisting of hard magnetic material powder and soft magnetic material powder; the hard magnetic material powder is selected from strontium ferrite magnetic powder and barium ferrite magnetic powder, and the soft magnetic material powder is selected from iron, cobalt and nickel powders;
wherein the matrix component is at least one selected from polyethylene (PE), polypropylene (PP), ethylene vinyl acetate (EVA), ethylene acrylic acid copolymer (EAA), ethylene ethyl acrylate (EEA), thermoplastic elastomer (TPE), thermoplastic polyurethanes (TPU), styrene-ethylene-butylene-styrene (SEBS), and styrene-butadiene-styrene (SBS).
2. The plastic magnetic material according to claim 1 , wherein the printable layer is selected from the group consisting of paper, printable and writable plastic film, textile film, printable coating, and combinations thereof.
3. The plastic magnetic material according to claim 1 , further comprising a release film arranged on a second side of the organic silicon pressure sensitive adhesive layer, opposite the first side.