Three-dimensional printing methods and materials for making dental products
The present invention provides a three-dimensional printing article for making dental products and the preparation method thereof, which comprises: Ethoxylated bisphenol A dimethacrylate, Diurethane dimethacrylate, Triethylene glycol dimethacrylate, and Diphenyl (2,4,6-trimethylbenzoyl) phosphine oxide. It not only improves the present time-consuming and labor-intensive dental device making, but also can be used in mass production of dental devices.
1. A three-dimensional printing article for making dental products, comprising a composition, wherein the composition comprises:
an Ethoxylated bisphenol A dimethacrylate, a Diurethane dimethacrylate and a Triethylene glycol dimethacrylate with 20 to 80 wt %:0 to 75 wt %:0 to 10 wt % of the composition;
a toner, wherein the toner consists of ferrihydrite (III) with 0.01 to 0.05 wt % of the composition, or iron trioxide with 0.001 to 0.005 wt % of the composition; and
a photo-initiator, wherein the photo-initiator is with 0.01 to 10 wt % of the composition.
2. The article of claim 1 , wherein the composition further comprising: a Trimethylolpropane triacrylate (TMPTA) with 0 to 10 wt % of the compound.
3. The article of claim 1 , wherein the Ethoxylated bisphenol A Dimethacrylate has a chemical formula as the following:
and has two ethoxyl chains with n, m=2, 4 or 10.
4. The article of claim 1 , wherein the photo-initiator is Diphenyl (2, 4, 6-trimethylbenzoyl) phosphine oxide (TPO).
5. The article of claim 1 , wherein the composition further comprises a photoresist, wherein the photoresist consists of silicon dioxide or silylated silicon dioxide with 0.1 to 10 wt % of the composition, and titanium dioxide with 0.01 to 1 wt % of the composition.
6. A method for preparing an article of claim 1 , wherein the method composing:
(a) mixing an Ethoxylated bisphenol A dimethacrylate, a Diurethane dimethacrylate, and a Triethylene glycol dimethacrylate to form a compound at room temperature with 20 to 80 wt %:0 to 75 wt %:0 to 10 wt % of the composition,
(b) adding a toner and a photo-initiator to the composition, then mixing to form an article of claim 1 , wherein the photo-initiator is with 0.01 to 10 wt % of the compound.
7. The method of claim 6 , wherein the step (a) further comprising:
(a1) adding a Trimethylolpropane triacrylate (TMPTA), with 0 to 10 wt %:of the compound.
8. The method of claim 6 , wherein the step (a) further comprising:
(a2) adding a photoresist or a toner into the compound, wherein the photoresist wherein the photoresist is consisted of silicon dioxide or silylated silicon dioxide with 0.1 to 10 wt % of the compound, and titanium dioxide with 0.01 to 1 wt % of the compound, wherein the toner is consisted of ferrihydrite (III) with 0.01 to 0.05 wt % of the compound, or iron trioxide with 0.001 to 0.005 wt % of the compound.
9. A method for preparing a dental prosthesis, wherein the method comprising:
(a) pouring an article of claim 1 into a container;
(b) obtaining a plurality of continuously sectional drawings of a dental prosthesis simple, wherein there is a sectional distance of the dental prosthesis simple between each drawing;
(c) choosing the top of the drawings, forming a sheet model as the chosen drawing through focusing an intensive irradiation light source on the bottom of the container; and
(d) moving the sheet model upward for the sectional distance, and repeating step (c) through choosing the next of the drawings until the bottom of the drawings, each of the sheet models is sequentially stacked to form the dental prosthesis.
10. The method of claim 9 , wherein in the step (c), the intensive irradiation light source is with wavelength ranging from 256 to 500 nm focusing on the bottom of the container for 1˜8 seconds.