Graphene oxide-based porous 3D mesh
A method of making a porous three-dimensional graphene mesh includes combining a graphene-containing material and a polymer having a plurality of hydroxyl groups in an alcohol solvent to form a mixture, adding a salt to the mixture, heating the mixture to form a gel, and washing the gel with water to remove the salt from the gel, leaving behind stable pores to form a scaffold. A three-dimensional porous graphene mesh includes a graphene-containing material and a polymer. The polymer is crosslinked with the graphene-containing material such that the Young's Modulus of the mesh is at least about 5 GPa.
1. A method of making a porous three-dimensional graphene mesh, the method comprising:
combining a graphene-containing material and polyethylene glycol (PEG) having a molecular weight between 6000 daltons and 8000 daltons in an alcohol solvent to form a mixture, wherein the alcohol solvent is methanol, ethanol, propanol, butanol, or pentanol;
adding sodium chloride (NaCl) to the mixture such that the ratio of graphene-containing material to NaCl is 1:12 or greater;
heating the mixture to form a gel to a temperature between about 60° C. and about 85° C. for between about 1 hour and about 36 hours; and
washing the gel with water to remove the NaCl from the gel leaving behind stable pores to form a scaffold having a porosity between about 50% and about 90% and an average pore size between about 5 μm and about 50 μm.
2. The method of claim 1 , further comprising:
drying the gel at a temperature between about 40° C. and about 70° C. for between about 1 hour and about 24 hours.
3. The method of claim 2 , wherein the alcohol solvent is methanol, ethanol, propanol, butanol, or pentanol.