Wrought machinable brass alloy
A wrought machinable low copper, silicon, zinc alloy having a copper content between about 66 weight percent and about 69 weight percent and wherein the silicon content is between about 1.53 weight percent and about 2.0 weight percent.
1. A wrought machinable, dezincification-resistant, low lead, low copper, silicon, zinc alloy consisting of between about 66 weight percent and 69 weight percent copper; greater than 1.53 weight percent and less than 2 weight percent silicon wherein the silicon content further satisfies the equation 0.167*Cu-9.28>Si>0.132*Cu-7.66; up to about 0.25 weight percent lead; up to about 0.15 weight percent phosphorus; up to about 0.5 weight percent iron; up to about 1.2 weight percent tin; up to about 2.5 weight percent aluminum; up to about 0.25 weight percent nickel; up to about 0.25 weight percent cobalt; up to about 0.15 weight percent arsenic; up to about 0.15 weight percent antimony; up to about 0.25 weight percent bismuth; up to about 0.25 weight percent selenium; up to 0.25 weight percent sulfur; and at least one from group consisting of: up to 0.4 weight percent tellurium; up to 0.1 weight percent zirconium; and up to 0.2 weight percent chromium; and the balance zinc and unavoidable impurities, wherein the alloy has been worked and heated sufficiently to produce a microstructure with a corrosion penetration ≤200 μm tested according to ISO 6509 Protocol.
2. The wrought machinable, dezincification-resistant, low lead, low copper, silicon, zinc alloy of claim 1 including zirconium at least 0.0005% weight percent.
3. The wrought machinable, dezincification-resistant, low lead, low copper, silicon, zinc alloy of claim 1 including chromium at least 0.01% weight percent.
4. The wrought machinable, dezincification-resistant, low lead, low copper, silicon, zinc alloy of claim 1 including tellurium metal at at least 0.02% weight percent.
5. A wrought machinable, dezincification-resistant, low lead, low copper, silicon, zinc alloy consisting of between about 66 weight percent and 69 weight percent copper; greater than 1.53 weight percent and less than 2 weight percent silicon wherein the silicon content further satisfies the equation 0.167*Cu-9.28>Si>0.132*Cu-7.66; up to about 0.25 weight percent lead; up to about 0.15 weight percent phosphorus; up to about 0.5 weight percent iron; up to about 1.2 weight percent tin; and other alloying elements each in an amount less than 0.1 weight percent, that do not materially affect corrosion resistance relative to an alloy without the alloying element and the balance zinc and unavoidable impurities, wherein the alloy has been worked and heated sufficiently to produce a microstructure with a corrosion penetration ≤200 μm tested according to ISO 6509 Protocol.