Release resistant moisture absorbent for automobile lamp, and moisture absorbent product comprising the same
Provided are a release resistant moisture absorbent being environment-friendly and having excellent moisture absorbency and release resistance, and a moisture absorbent product comprising the same. The release resistant moisture absorbent of the present invention has an excellent moisture absorption rate, and also excellent release resistance in a high temperature and low humidity condition which is a driving environment of an automobile lamp, and thus, may be usefully used for an automobile lamp.
1. A moisture absorbent product consisting essentially of a release resistant moisture absorbent consisting essentially of:
(A) a moisture absorbent material consisting of at least one selected from the group consisting of magnesium chloride, calcium chloride, and sodium carbonate;
(B) a curable inorganic material consisting of at least one selected from the group consisting of calcium oxide, magnesium oxide having a particle size of 20 to 80 mesh, and magnesium oxide having a particle size of 200 to 500 mesh; and
(C) an additive consisting of at least one polymer wax selected from the group consisting of polyethylene wax, polypropylene wax, polyamide wax, carnauba wax, paraffin wax, and polytetrafluoroethylene wax, and optionally at least one material selected from the group consisting of a low-density polyethylene resin and metal stearate;
wherein the release resistant moisture absorbent is granule-shaped or powder-shaped; and
wherein the release resistant moisture absorbent is filled in an air permeable packaging material which is in a thermally laminated form comprising at least two selected from the group consisting of high-density polyethylene (HDPE) non-woven fabric, a high-density polyethylene (HDPE) film, low-density polyethylene (LDPE) non-woven fabric and a low-density polyethylene (LDPE) film.
2. The moisture absorbent product of claim 1 , wherein 10 wt % to 40 wt % of (A) the moisture absorbent material; 10 wt % to 60 wt % of (B) the curable inorganic material; and 3 wt % to 70 wt % of (C) the additive are comprised in the release resistant moisture absorbent.
3. The moisture absorbent product of claim 1 , wherein the release resistant moisture absorbent is for an automobile lamp.
4. The moisture absorbent product of claim 1 , wherein the low-density polyethylene resin has a melt index according to ASTM D1238 of 5 to 30 g/10 min.
5. The moisture absorbent product of claim 1 , wherein the metal stearate is at least one selected from the group consisting of calcium stearate and magnesium stearate.
6. A release resistant moisture absorbent being granule-shaped and consisting essentially of:
(A) a moisture absorbent material consisting of at least one selected from the group consisting of magnesium chloride, calcium chloride, and sodium carbonate;
(B) a curable inorganic material consisting of at least one selected from the group consisting of calcium oxide, magnesium oxide having a particle size of 20 to 80 mesh, and magnesium oxide having a particle size of 200 to 500 mesh; and
(C) an additive consisting of at least one polymer wax selected from the group consisting of polyethylene wax, polypropylene wax, polyamide wax, carnauba wax, paraffin wax, and polytetrafluoroethylene wax, and optionally at least one material selected from the group consisting of a low-density polyethylene resin and metal stearate.