Polyethylene polymer powder and method of producing same
Provided are a polyethylene polymer powder and method of producing the same that can improve molding efficiency while maintaining high levels of molded product strength and wear resistance. The polyethylene polymer powder comprises an ethylene homopolymer or copolymer and has an intrinsic viscosity IV of at least 12 dL/g and not more than 35 dL/g, a melting peak full width at half maximum of at least 2° C. and not more than 7° C., a span (laser particle size distribution measurement) of at least 0.9 and not more than 2, and an α-olefin content of 0 mol % to not more than 1.50 mol %. The method of producing this polyethylene polymer powder includes polymerizing ethylene or ethylene and an α-olefin by slurry polymerization using a loop reactor. In the polymerizing, supply of a solvent and ethylene or supply of a solvent, ethylene, and an α-olefin is performed by a plurality of supply lines.
1. A polyethylene polymer powder comprising an ethylene homopolymer or a copolymer of ethylene and an α-olefin having a carbon number of at least 3 and not more than 8, wherein
the polyethylene polymer powder has an intrinsic viscosity IV of at least 12 dL/g and not more than 35 dL/g as measured at 135° C. in decalin solvent,
the polyethylene polymer powder has a melting peak full width at half maximum of at least 2° C. and not more than 7° C. as measured by differential scanning calorimetry at a heating rate of 10° C./min,
the polyethylene polymer powder has a span of at least 0.9 and not more than 2 as determined by laser particle size distribution measurement in methanol, and
the polyethylene polymer powder has an α-olefin content of 0 mol % to not more than 1.50 mol % as measured by 13 C-NMR.
2. The polyethylene polymer powder according to claim 1 , wherein
the polyethylene polymer powder has a heat of fusion ΔH1 of at least 100 J/g and not more than 200 J/g as measured by differential scanning calorimetry at a heating rate of 10° C./min, and
a temperature at which 5% heat of fusion of the heat of fusion ΔH1 is reached is at least 90° C. and not higher than 120° C.
3. The polyethylene polymer powder according to claim 1 for a compression molded product.
4. The polyethylene polymer powder according to claim 1 for a prosthetic joint.
5. A prosthetic joint comprising a crosslinked molded product obtained through γ-ray irradiation of a molded product of the polyethylene polymer powder according to claim 1 .
6. A method of producing the polyethylene polymer powder according to claim 1 , comprising:
polymerizing ethylene or ethylene and an α-olefin by slurry polymerization using a loop reactor, wherein
in the polymerizing, supply of a solvent and ethylene or supply of a solvent, ethylene, and an α-olefin is performed by a plurality of supply lines.
7. The polyethylene polymer powder according to claim 2 for a compression molded product.
8. The polyethylene polymer powder according to claim 2 for a prosthetic joint.
9. A prosthetic joint comprising a crosslinked molded product obtained through γ-ray irradiation of a molded product of the polyethylene polymer powder according to claim 2 .
10. A method of producing the polyethylene polymer powder according to claim 2 , comprising:
polymerizing ethylene or ethylene and an α-olefin by slurry polymerization using a loop reactor, wherein
in the polymerizing, supply of a solvent and ethylene or supply of a solvent, ethylene, and an α-olefin is performed by a plurality of supply lines.