Lithium-sulfur battery with polyanthraquinone binder
A cathode for a lithium-sulfur (Li—S) battery is described herein, which comprises elemental sulfur (e.g., S 8 ) and an electroactive polyanthraquinone-containing binder. In some embodiments, the cathode also includes a conductive carbon material in addition to the sulfur and binder. Also described herein is a Li—S battery comprising the cathode, in combination with a metallic lithium-containing anode, a lithium conductive separator membrane between the anode and the cathode, and a liquid electrolyte comprising a lithium salt dissolved in a non-aqueous organic solvent.
1. A lithium-sulfur (Li—S) battery cathode comprising elemental sulfur dispersed in a binder comprising 2,6-polyanthraquinone.
2. The cathode of claim 1 , further comprising a current collector contacting the sulfur and the binder.
3. The cathode of claim 1 , wherein the elemental sulfur and the binder are coated on an aluminum current collector.
4. The cathode of claim 1 , wherein the cathode further comprises a carbon material dispersed in the binder.
5. The cathode of claim 1 , wherein the 2,6-polyanthraquinone has a number average molecular weight of about 60 kDa to 80 kDa and a polydispersity index of about 2 to about 2.2, as determined by reduction of the 2,6-polyanthraquinone with about 2 equivalents of lithium naphthalenide per anthraquinone unit thereof, followed by gel permeation size exclusion chromatography using a chromatography medium comprising a highly cross-linked polystyrene-divinylbenzene gel and narrow dispersity polystyrene standards with tetrahydrofuran as eluent.
6. The cathode of claim 1 , wherein the 2,6-polyanthraquinone comprises about 50 to about 66 percent by weight (wt %) of the binder.
7. The cathode of claim 1 , wherein the 2,6-polyanthraquinone comprises about 50 wt % of the binder.
8. The cathode of claim 1 , wherein the binder further comprises at least one other binder compound in combination with the 2,6-polyanthraquinone.
9. The cathode of claim 8 , wherein the at least one other binder compound comprises polyvinylidene difluoride.
10. The cathode of claim 1 , wherein the cathode comprises about 50 wt % of S 8 , about 20 to about 40 wt % of a carbon material, and about 10 to about 30 wt % of the binder.
11. A lithium-sulfur (Li—S) battery comprising:
(a) an anode comprising metallic lithium;
(b) a cathode comprising elemental sulfur dispersed in a binder comprising 2,6-polyanthraquinone;
(c) a porous separator membrane between the anode and the cathode; and
(d) a liquid electrolyte composition comprising a lithium salt dissolved in a non-aqueous organic solvent contacting the anode, the cathode, and the membrane.
12. The battery of claim 11 , wherein the cathode further comprises a current collector contacting the sulfur and the binder.
13. The battery of claim 11 , wherein the elemental sulfur and the 2,6-polyanthraquinone are coated on an aluminum current collector.
14. The battery of claim 11 , wherein the cathode further comprises a carbon material dispersed in the binder.
15. The battery of claim 11 , wherein the 2,6-polyanthraquinone has a number average molecular weight of about 60 kDa to 80 kDa and a polydispersity index of about 2 to about 2.2, as determined by reduction of the 2,6-polyanthraquinone with about 2 equivalents of lithium naphthalenide per anthraquinone unit thereof, followed by gel permeation size exclusion chromatography using a chromatography medium comprising a highly cross-linked polystyrene-divinylbenzene gel and narrow dispersity polystyrene standards with tetrahydrofuran as eluent.
16. The battery of claim 11 , wherein the 2,6-polyanthraquinone comprises about 50 to about 66 wt % of the binder.
17. The battery of claim 11 , wherein the 2,6-polyanthraquinone comprises about 50 wt % of the binder.
18. The battery of claim 11 , wherein the binder comprises at least one other binder compound in combination with the 2,6-polyanthraquinone.
19. The battery of claim 18 , wherein the at least one other binder compound comprises polyvinylidene difluoride.
20. The battery of claim 11 , wherein the cathode comprises about 50 wt % of S 8 , about 20 to about 40 wt % of a carbon material, and about 10 to about 30 wt % of the binder.