Coating for recyclable paper
The present disclosure relates to weatherproof or moisture-resistant writable or printable paper or paper-containing substrates, which includes recyclable cellulosic sheets coated with a coating layer. Sheets are suitable for writing and printing and are prepared by impregnantly coating a cellulosic substrate. In addition, a composition used for coating paper sheets and related substrates to obtain general-purpose weatherproof sheets comprising a substrate, a polymer, a cross-linking agent and methods for producing and using the same are disclosed. The sheets resist degradation, remain legible, can be written upon when wet, and are recyclable.
1. A recyclable sheet comprising:
a substrate consisting of a 24 pound short fiber recycled paper;
a coating layer formed by directly contacting and impregnantly covering at least one of the two sides of the substrate with a mixture comprising a styrene acrylic polymer and 3 wt % of a methylene diphenyl diisocyanate and polypropylene ether glycol based prepolymer as a cross-linking agent and having a viscosity less than 1900 cP after 7 hours of mixing; and
cross-links between:
i) a plurality of cellulose fibers;
ii) a plurality of cellulose fibers and the styrene acrylic polymer; and
iii) styrene acrylic polymer molecules,
wherein the degree of cross-linking is controlled such that the recyclable sheet having the cross-links is recyclable and has a wet strength of at least 2300 newtons and maintains a writability score of 9 on a scale of 0-10 after getting wet without ink feathering or paper tearing, wherein 0 denotes unacceptable writability and 10 denotes no wicking, smearing, or paper ripping during writing based on a test using oil based ink from a ballpoint pen.
2. The recyclable sheet of claim 1 , wherein the coating layer further comprises a second polymer.
3. The recyclable sheet of claim 2 , wherein the second polymer is a copolymer.
4. The recyclable sheet of claim 2 , wherein the second polymer is a polyacrylic polymer.
5. The recyclable sheet of claim 1 , wherein the density of the coating layer on the sheet ranges from about 0.5 grams per square meter of the sheet to about 10.0 grams per square meter of the sheet.
6. The recyclable sheet of claim 1 , wherein the coating layer has a moisture content less than 10% by weight based on the total weight of the coating layer.
7. The recyclable sheet of claim 1 , wherein the coating layer has a total polymer content of less than 85% by weight, based on the total weight of the coating layer.
8. The recyclable sheet of claim 1 , wherein the coating layer further comprises barium sulfate.
9. The recyclable sheet of claim 1 , wherein the coating layer further comprises a wax comprising a paraffin wax, a polypropylene-wax mixture, a polyethylene-wax mixture, carnauba wax, microcrystalline wax, montan wax, a Fisher-Tropsch wax, beeswax or mixtures thereof.
10. The recyclable sheet of claim 1 , wherein the recyclable sheet having the cross-links has the wet strength of at least 2900 newtons.
11. A method for forming a recyclable sheet, the method comprising:
i. providing a substrate consisting of a 24 pound short fiber recycled paper; and
ii. contacting the substrate with a composition comprising a mixture of styrene acrylic polymer and 3 wt % of a methylene diphenyl diisocyanate and polypropylene ether glycol based prepolymer as a cross-linking agent and having a viscosity less than 1900 cP after 7 hours of mixing thereby forming:
a) a coating layer; and
b) cross-links between:
i) a plurality of cellulose fibers;
ii) a plurality of cellulose fibers and the styrene acrylic polymer; and
iii) styrene acrylic polymer molecules,
wherein the degree of cross-linking is controlled such that the recyclable sheet having the cross-links is recyclable and has a wet strength of at least 2300 newtons and maintains a writability score of 9 on a scale of 0-10 after getting wet without ink feathering or paper tearing, wherein 0 denotes unacceptable writability and 10 denotes no wicking, smearing, or paper ripping during writing based on a test using oil based ink from a ballpoint pen.
12. The method of claim 11 , wherein the recyclable sheet having the cross-links has a wet strength of at least 2900 newtons.
13. The method of claim 11 , wherein the mixture further comprises a second polymer.
14. The method of claim 13 , wherein the second polymer is a copolymer.
15. The method of claim 13 , wherein the second polymer is a polyacrylic polymer.