Systems and methods of recovering precious metals and extracting copper from diverse substances
Disclosed is a method for extracting a desired metal contained in electronic waste having a substrate and desired metal integrally formed with copper, the method includes (a) contacting the electronic waste with a cupric amine solution to separate the desired metal integrally formed with copper from the substrate and the copper, and (b) optionally providing ultrasound energy at a frequency ranging from 15 to 45 KHz and at a temperature ranging from 45° C. to 60° C. thereby limiting metallic oxide(s) formation at a surface of a workface; and (c) etching the copper with the cupric amine solution at a temperature ranging from 45° C. to 60° C. for between 40 to 70 hours thereby releasing the desired metal from the substrate and the copper; (d) collecting the released desired metal of step (c).
1. A method for extracting a desired metal from a substance, the method comprising:
contacting the substance with a cupric amine solution to separate the desired metal from the substance;
providing ultrasound energy on a work face of the substance;
etching the substance with the cupric amine solution, thereby releasing the desired metal from the substance; and
collecting the released desired metal.
2. The method of claim 1 , wherein the substance includes integrated circuit boards, printed circuit boards, capacitors, metal fragments, large irregular granules, and small irregular granules.
3. The method of claim 2 , wherein the metal fragments have a copper content between 70-80%.
4. The method of claim 3 , further comprising leaching the fragments for 35-45 hours wherein 50-75% of the copper is removed from the fragments.
5. The method of claim 4 , further comprising isolating precious metals from the fragment after the copper has been removed.
6. The method of claim 5 , wherein precious metals include gold, platinum, silver, iridium, and palladium.
7. The method of claim 2 , wherein the large irregular granules weigh between 10-20 grams.
8. The method of claim 2 , wherein the small irregular granules weigh between 0.5 and 1.5 grams.
9. The method of claim 1 , further comprising flashing off any by-products having a melting point below the desired metal.
10. A method for extracting a desired metal contained in a substance, the method comprising:
contacting the substance with a cupric amine solution to separate the desired metal from the substance;
etching the substance with the cupric amine solution, thereby releasing the desired metal from the substance;
collecting the released desired metal; and
purifying the desired metal, thereby resulting in a concentrated form of the desired metal, wherein the desired metal includes at least one metal selected from the group consisting of gold, platinum, silver, iridium, and palladium.