Drug eluting medical implant
Disclosed are self-expanding medical implants for placement within a lumen of a patient. The implants comprise a woven or non-woven structure having a substantially tubular configuration, and are designed to be low-profile such that they are deliverable with a small diameter catheter. The implants have a high recoverability and desired mechanical properties.
1. A method of making a self-expanding implant, comprising: a) manufacturing a tubular structure to a first diameter, said structure comprising at least one strand comprising a first polymer; and b) coating said tubular structure with a second polymer so that it at least partially coats said strand, said second polymer comprising an elastomeric polymer that when compressed or elongated, applies a force to the tubular structure that acts in favor of radial expansion, thereby making a self-expanding implant.
2. The method of claim 1 , further comprising the step c) collapsing said self-expanding implant to a second, reduced diameter so as to create a crimped implant.
3. The method of claim 2 , further comprising the step d) placing said crimped implant in a catheter.
4. The method of claim 3 , further comprising the step e) extruding said crimped implant from said catheter such that said implant self-expands towards the first diameter.
5. The method of claim 4 , wherein said implant self-expands to at least 80% of said first diameter.
6. The method of claim 4 , wherein said implant self-expands to at least 90% of said first diameter.
7. The method of claim 4 , wherein said implant self-expands to at least 95% of said first diameter.
8. The method of claim 1 , wherein said first polymer is biodegradable.
9. The method of claim 1 , wherein said first polymer comprises poly(lactic acid co-glycolic acid).
10. The method of claim 1 , wherein said second polymer comprises an elastic segment having a glass transition temperature less than about 5° C.
11. The method of claim 1 , wherein said second polymer is poly(lactic acid-co-caprolactone).
12. The method of claim 1 , wherein said poly(lactic acid-co-caprolactone) is crosslinked with hexamethylene diisocyanate.
13. The method of claim 1 , wherein the crosslinked density of the elastomeric polymer is optimized with hexamethylene diisocyante, or other crosslinkers or in combination with chain terminators.
14. The method of claim 1 , wherein said tubular structure of step a) is a braided structure comprising a plurality of strands.
15. The method of claim 14 , wherein said braided structure comprises between 16 and 48 strands.
16. The method of claim 14 , wherein said strands form an average braid angle of between about 90 degrees and about 135 degrees.
17. The method of claim 1 , wherein the second polymer increases the mass of said self-expanding implant by at least 15 percent.
18. The method of claim 1 , further comprising the step of at least partially coating said second polymer with a third polymer.
19. The method of claim 18 , wherein said third polymer comprises a therapeutic agent.
20. The method of claim 19 , further comprising the step of at least partially coating said third polymer with a topcoat, said topcoat regulating the delivery of the therapeutic agent.