Sintered body and cutting tool
A sintered body includes cubic boron nitride grains as hard phase grains, and has a thermal conductivity of less than 20 W·m −1 ·K −1 , for cutting a nickel-based heat-resistant alloy formed of crystal grains having a coarse grain size represented by a grain size number of 5 or less defined by ASTM standard E112-13. A cutting tool includes this sintered body. Accordingly, the sintered body having high fracture resistance in addition to high wear resistance, as well as the cutting tool including the sintered body are provided.
1. A method for manufacturing a cut material, the method comprising:
preparing a nickel-based heat-resistant alloy formed of crystal grains having a coarse grain size represented by a grain size number of 5 or less defined by American Society for Testing and Materials standard E112-13; and
cutting the nickel-based heat-resistant alloy by using a sintered body comprising cubic boron nitride grains as hard phase grains and having a thermal conductivity of less than 15 W·m −1 ·K −1 , wherein
the sintered body further comprises:
a binder;
different-type hard phase grains including at least one selected from the group consisting of silicon nitride, SiAlON, and alumina, as the hard phase grains other than the cubic boron nitride grains, and
a ratio V BN /V H of a volume V BN of the cubic boron nitride grains to a volume V H of the different-type hard phase grains is not less than 0.5 and not more than 1.5.
2. The method for manufacturing the cut material according to claim 1 , wherein
the SiAlON includes cubic SiAlON.
3. The method for manufacturing the cut material according to claim 2 , wherein
the SiAlON further includes at least one of α-SiAlON and β-SiAlON, and
a peak intensity ratio Rc of an intensity at an X-ray diffraction main peak of the cubic SiAlON to a sum of respective intensities at respective X-ray diffraction main peaks of the α-SiAlON, the β-SiAlON, and the cubic SiAlON is not less than 20%.
4. The method for manufacturing the cut material according to claim 1 , wherein
the binder includes at least one kind of binder selected from the group consisting of at least one kind of element out of titanium, zirconium, aluminum, nickel, and cobalt, nitrides, carbides, oxides, carbonitrides, and borides of the elements, and solid solutions thereof.
5. The method for manufacturing the cut material according to claim 1 , wherein
a content of the hard phase grains in the sintered body is not less than 60 vol % and not more than 90 vol %.
6. The method for manufacturing the cut material according to claim 1 , wherein
the sintered body has a Vickers hardness of not less than 20 GPa.
7. The method for manufacturing the cut material according to claim 1 , wherein
the nickel-based heat-resistant alloy includes nickel of not less than 50 mass % and not more than 55 mass %, chromium of not less than 17 mass % and not more than 21 mass %, niobium of not less than 4.75 mass % and not more than 5.50 mass %, molybdenum of not less than 2.80 mass % and not more than 3.30 mass %, and iron of not less than 12 mass % and not more than 24 mass %.
8. The method for manufacturing the cut material according to claim 1 , wherein
the cutting of the nickel-based heat-resistant alloy is performed by using a cutting tool comprising the sintered body.