Short carbon fiber-reinforced composite material and method for producing same

1. A short carbon fiber-reinforced composite material, comprising a base material part and at least one sliding part contacting the base material part, wherein:

each of the base material part and the sliding part has a plurality of short carbon fiber bundles in which at least a part thereof has been converted into SiC, and a SiC matrix present among the plurality of short carbon fiber bundles, as constituent components; and

the short carbon fiber bundles of the sliding part have a SiC conversion higher than that of the short carbon fiber bundles of the base material part,

wherein the SiC conversion of the short carbon fiber bundles of the sliding part is 45% or more and 80% or less, and the SiC conversion of the short carbon fiber bundles of the base material part is 5% or more and 25% or less.

2. A method for producing a short carbon fiber-reinforced composite material according to claim 1 , comprising:

a step of mixing a phenol resin with short carbon fiber bundles for a base material part, wherein the short carbon fiber bundles are carbon-coated with a pitch, to obtain a mixture for a base material part;

a step of mixing SiC and a phenol resin with short carbon fiber bundles for a sliding part, wherein the short carbon fiber bundles are resin-coated with a phenol resin, to obtain a mixture for a sliding part;

a step of placing the mixture for a sliding, part and the mixture for a base material part in a molding die, followed by a pressure-molding under heating to obtain a cured body;

a step of baking the cured body at 2000° C. or higher to obtain a baked body; and

a step of infiltrating the baked body with silicon by a silicon melt infiltration process at about 1500° C. in vacuum.