Oil, grease, and moisture resistant paperboard having a natural appearance
A coated paperboard having a natural appearance is disclosed which includes a barrier coating containing substantially no fluorochemical or wax, exhibiting good resistance to oil, grease, and moisture and having no tendency toward blocking.
1. A coated paperboard comprising:
an unbleached paperboard substrate having a first side and a second side; and
a first coating in contact with the first side, the first coating having a coat weight from about 6 to 14 lbs per 3000 ft 2 and comprising binder and pigment having a binder to pigment ratio in a range of 30 to 50 parts binder per 100 parts pigment, by weight, and substantially no fluorochemical or wax;
wherein the coated paperboard provides barrier properties to at least one of oil, grease, and moisture;
wherein the coated paperboard is repulpable to the extent that after repulping the percentage accepts is at least 95%; and
wherein the coated paperboard has a natural appearance wherein the substrate fibers are substantially visible through the first coating.
2. The coated paperboard of claim 1 , wherein the binder to pigment ratio in the first coating is in a range of 35 to 45 parts binder per 100 parts pigment, by weight.
3. The coated paperboard of claim 1 , wherein the binder in the first coating comprises at least one of styrene butadiene copolymer, protein, styrene acrylate copolymer, polyvinyl acetate, and vinyl acrylics copolymer.
4. The coated paperboard of claim 1 , further comprising a second coating applied over the first coating, the second coating having a coat weight such that the total coat weight of the first and second coatings is about 10 to 20 lbs per 3000 ft 2 and comprising binder and pigment, and substantially no fluorochemical or wax.
5. The coated paperboard of claim 4 , wherein the binder to pigment ratio in the second coating is in a range of 30 to 50 parts binder per 100 parts pigment, by weight.
6. The coated paperboard of claim 4 , wherein the binder in the second coating comprises at least one of styrene butadiene copolymer, protein, styrene acrylate copolymer, polyvinyl acetate, and vinyl acrylics copolymer.
7. The coated paperboard of claim 4 , wherein the 3M kit test value is at least 10.
8. The coated paperboard of claim 1 , wherein the 3M kit test value is at least 4.
9. The coated paperboard of claim 1 , wherein the coated paperboard has a 30-minute oil Cobb test of at most 3 grams per square meter.
10. The coated paperboard of claim 9 , wherein the coated paperboard has a 30-minute oil Cobb test of at most 1 gram per square meter.
11. The coated paperboard of claim 1 , wherein the coated paperboard has a water vapor transmission rate of less than 500 grams per square meter per day.
12. The coated paperboard of claim 11 , wherein the coated paperboard has a water vapor transmission rate of less than 300 grams per square meter per day.
13. The coated paperboard of claim 11 , wherein the coated paperboard has a water vapor transmission rate of less than 200 grams per square meter per day.
14. The coated paperboard of claim 1 , having no tendency toward blocking after being held for 24 hours at 50° C. at a pressure of 100 psi.
15. The coated paperboard of claim 1 , wherein the coated paperboard is repulpable to the extent that after repulping the percentage accepts is at least 98%.
16. The coated paperboard of claim 1 , wherein the pigment comprises at least one of clay and calcium carbonate.
17. The coated paperboard of claim 16 , wherein the pigment comprises a clay having a particle size of 90-100%<2 microns.
18. The coated paperboard of claim 16 , wherein the pigment comprises a platy clay.
19. The coated paperboard of claim 16 , wherein the pigment comprises ground calcium carbonate having a particle size of at least 60%<2 microns.
20. A coated paperboard comprising:
an unbleached paperboard substrate having a first side and a second side;
a first coating in contact with the first side, the first coating having a coat weight from about 6 to 14 lbs per 3000 ft 2 and comprising binder and pigment having a binder to pigment ratio in a range of 30 to 50 parts binder per 100 parts pigment, by weight, and substantially no fluorochemical or wax;
wherein the coated paperboard provides barrier properties to at least one of oil, grease, and moisture;
wherein the coated paperboard is repulpable to the extent that after repulping the percentage accepts is at least 95%; and
wherein the first side of the coated paperboard has an L-a-b color space value in which L is less than 72.
21. The coated paperboard of claim 20 , wherein L is less than 62.
22. The coated paperboard of claim 20 , wherein L is less than 60.
23. The coated paperboard of claim 20 , further comprising a second coating applied over the first coating, the second coating having a coat weight such that the total coat weight of the first and second coatings is about 10 to 20 lbs per 3000 ft 2 and comprising binder and pigment, and substantially no fluorochemical or wax.
24. A coated paperboard comprising:
an unbleached paperboard substrate having a first side and a second side;
a first coating in contact with the first side, the first coating having a coat weight from about 6 to 14 lbs per 3000 ft 2 and comprising binder and pigment having a binder to pigment ratio in a range of 30 to 50 parts binder per 100 parts pigment, by weight, and substantially no fluorochemical or wax;
wherein the coated paperboard provides barrier properties to at least one of oil, grease, and moisture;
wherein the coated paperboard is repulpable to the extent that after repulping the percentage accepts is at least 95%; and
wherein the first side of the coated paperboard has an L-a-b color space value in which b is greater than 6.
25. The coated paperboard of claim 24 , wherein b is greater than 9.5.
26. The coated paperboard of claim 24 , further comprising a second coating applied over the first coating, the second coating having a coat weight such that the total coat weight of the first and second coatings is about 10 to 20 lbs per 3000 ft 2 and comprising binder and pigment, and substantially no fluorochemical or wax.