Antimicrobial coatings comprising quaternary silanes
A method of preparing an antimicrobial coating comprises coating a surface with an aqueous mixture of 3-(trihydroxysilyl)propyl dimethyloctadecyl ammonium chloride, 3-chloropropyltrimethoxysilane, and triethanolamine and then coating the surface with an aqueous titanyl sol-gel solution comprising an aqueous mixture of peroxotitanium acid and peroxo-modified anatase sol overtop of the silane to form the antimicrobial coating. The antimicrobial coating exhibits residual antimicrobial efficacy against E. coli and S. epidermidis after water rinsing or after abrasion. The use of 3-chloropropyltrimethoxysilane was found to improve storage stability of the quaternary silane composition and the durability of the antimicrobial coating.
1. A method of preparing an antimicrobial coating on a portion of a surface, the method comprising:
disposing an aqueous antimicrobial coating composition comprising from about 0.5 wt. % to about 1.0 wt. % 3-(trihydroxysilyl)propyl dimethyloctadecyl ammonium chloride and from about 0.01 wt. % to about 0.10 wt. % triethanolamine, remainder water, on the portion of the surface; and
disposing an aqueous titanyl sol-gel on the portion of the surface overtop of the aqueous antimicrobial coating composition,
wherein the antimicrobial coating thus formed exhibits residual antimicrobial efficacy against E. coli and S. epidermidis after exposure to water rinsing or mechanical abrasion.
2. The method of claim 1 , wherein the titanyl sol-gel comprises 0.85 wt. % peroxotitanium acid and peroxo-modified anatase sol mixture, with the remainder of the sol-gel being water.
3. The method of claim 1 , wherein the aqueous antimicrobial coating composition further comprises 3-chloropropyltrimethoxysilane.
4. The method of claim 3 , wherein the aqueous antimicrobial coating composition comprises about 0.75 wt. % 3-(trihydroxysilyl)propyl dimethyloctadecyl ammonium chloride, about 0.06 wt. % 3-chloropropyltrimethoxysilane, and about 0.045 wt. % triethanolamine, with the remainder of the aqueous antimicrobial coating composition being water.
5. The method of claim 4 , wherein the resulting antimicrobial coating retains about 63% of its weight after 10-cycles of abrasion in a straight-line washability machine equipped with a 1 kg weighted boat wrapped in a water-moisturized wiper.
6. The method of claim 4 , wherein the resulting antimicrobial coating retains about 67% of its weight after 30-cycles of abrasion in a straight-line washability machine equipped with a 1 kg weighted boat wrapped in a water-moisturized wiper.
7. The method of claim 3 , wherein the aqueous antimicrobial coating composition comprises about 0.75 wt. % 3-(trihydroxysilyl)propyl dimethyloctadecyl ammonium chloride, about 0.12 wt. % 3-chloropropyltrimethoxysilane, and about 0.045 wt. % triethanolamine, with the remainder of the aqueous antimicrobial coating composition being water.
8. The method of claim 7 , wherein the resulting antimicrobial coating retains about 77% of its weight after 10-cycles of abrasion in a straight-line washability machine equipped with a 1 kg weighted boat wrapped in a water-moisturized wiper.
9. The method of claim 7 , wherein the resulting antimicrobial coating retains about 76.5% of its weight after 30-cycles of abrasion in a straight-line washability machine equipped with a 1 kg weighted boat wrapped in a water-moisturized wiper.
10. A method of preparing an antimicrobial coating on a portion of a surface, the method comprising:
spray coating an aqueous antimicrobial coating composition comprising about 0.75 wt. % 3-(trihydroxysilyl)propyl dimethyloctadecyl ammonium chloride, about 0.06 wt. % 3-chloropropyltrimethoxysilane, and about 0.045 wt. % triethanolamine, remainder water, on the portion of the surface;
allowing the aqueous antimicrobial coating composition to visibly dry on the portion of the surface;
disposing an aqueous titanyl sol-gel comprising about 0.85 wt. % of a mixture of peroxotitanium acid and peroxo-modified anatase sol in water on the portion of the surface overtop of the dried aqueous antimicrobial coating composition; and
allowing the aqueous sol-gel to dry to provide the antimicrobial coating.
11. The method of claim 10 , wherein the resulting antimicrobial coating exhibits residual antimicrobial efficacy against E. coli and S. epidermidis after water rinsing or after mechanical abrasion.
12. The method of claim 10 , wherein the resulting antimicrobial coating retains about 48% of its weight after exposure to water rinsing.
13. The method of claim 10 wherein the resulting antimicrobial coating retains about 63% of its weight after exposure to 10-cycles of abrasion in a straight-line washability machine equipped with a 1 kg weighted boat wrapped in a water-moisturized wiper.
14. The method of claim 10 , wherein the resulting antimicrobial coating retains about 67% of its weight after 30-cycles of abrasion in a straight-line washability machine equipped with a 1 kg weighted boat wrapped in a water-moisturized wiper.
15. A method of preparing an antimicrobial coating on a portion of a surface, the method comprising:
spray coating an aqueous antimicrobial coating composition comprising about 0.75 wt. % 3-(trihydroxysilyl)propyl dimethyloctadecyl ammonium chloride, about 0.12 wt. % 3-chloropropyltrimethoxysilane, and about 0.045 wt. % triethanolamine, remainder water, on the portion of the surface;
allowing the aqueous antimicrobial coating composition to visibly dry on the portion of the surface;
disposing an aqueous titanyl sol-gel comprising about 0.85 wt. % of a mixture of peroxotitanium acid and peroxo-modified anatase sol in water on the portion of the surface overtop of the dried aqueous antimicrobial coating composition; and
allowing the aqueous sol-gel to dry to provide the antimicrobial coating.
16. The method of claim 15 , wherein the resulting antimicrobial coating exhibits residual antimicrobial efficacy against E. coli and S. epidermidis after water rinsing or after mechanical abrasion.
17. The method of claim 15 , wherein the resulting antimicrobial coating retains about 56% of its weight after exposure to water rinsing.
18. The method of claim 15 , wherein the resulting antimicrobial coating retains about 77% of its weight after exposure to 10-cycles of abrasion in a straight-line washability machine equipped with a 1 kg weighted boat wrapped in a water-moisturized wiper.
19. The method of claim 15 , wherein the resulting antimicrobial coating retains about 76.5% of its weight after exposure to 30-cycles of abrasion in a straight-line washability machine equipped with a 1 kg weighted boat wrapped in a water-moisturized wiper.
20. A method of preparing an antimicrobial coating on a portion of a surface, the method comprising:
disposing an aqueous antimicrobial coating composition comprising 3-(trihydroxysilyl)propyl dimethyloctadecyl ammonium chloride and triethanolamine on the portion of the surface; and
disposing an aqueous titanyl sol-gel on the portion of the surface overtop of the aqueous antimicrobial coating composition, the aqueous titanyl sol-gel comprising 0.85 wt. % peroxotitanium acid and peroxo-modified anatase sol mixture, with the remainder of the sol-gel being water,
wherein the antimicrobial coating thus formed exhibits residual antimicrobial efficacy against E. coli and S. epidermidis after exposure to water rinsing or mechanical abrasion.