Method of producing limestone-simulating concrete
A new process for creating a decorative surface on a cast concrete tile. A mold is prepared by coating with mold release. An aggregate of water, coloring dye, sand, Portland cement, and preferably filler material such as pea gravel is pre-mixed. Baking soda is mixed with a significant volume of water to create a high-viscosity paste. The paste preferably has a high solid to liquid ratio so that it can be crumbled into baking soda clumps of various sizes. The dampened baking soda clumps are sprinkled randomly onto the bottom surface of the mold (which will bear against what becomes the top surface of the cast tile). The pre-mixed aggregate is then added to the mold. Once the aggregate is cured, the cast concrete tile is removed. The baking soda clumps create complex voids in the tile's upper surface, producing a surface texture similar to limestone.
1. A method of producing a concrete casting having a stone-mimicking surface, comprising:
a. providing a concrete mold having a base, encircling side walls, and an open top;
b. providing a mixed aggregate, including,
i. sand,
ii. cement,
iii. coloring dye, and
iv. water;
c. providing a high-viscosity paste of water infused baking soda wherein said paste includes a specific volumetric baking soda to water ratio;
d. providing a flexible paste clump mold having multiple cavities, wherein said flexible paste clump mold is made of a sheet of flexible material;
e. squeegeeing said high-viscosity paste into said cavities within said flexible paste clump mold to create molded paste clumps;
f. inverting said flexible paste clump mold and flexing said flexible paste clump mold to eject said molded paste clumps;
g. randomly distributing said molded paste clumps on said base of said concrete mold;
h. filling said concrete mold with said aggregate;
i. allowing said aggregate to harden into a solid, thereby forming said casting; and
j. removing said casting from said mold.
2. A method of producing a concrete casting as recited in claim 1 , wherein said paste includes a volumetric baking soda to water ratio between about 2.5 to 1 and about 5.0 to 1.
3. A method of producing a concrete casting as recited in claim 1 , wherein said high-viscosity paste comprises a volumetric baking soda to water ratio between 3.75 to 1 and 5 to 1.
4. A method of producing a concrete casting as recited in claim 3 , wherein said high-viscosity paste comprises a volumetric baking soda to water ratio between 4.25 to 1 and 4.75 to 1.
5. A method of producing a concrete casting as recited in claim 1 , further comprising removing said baking soda clumps from said completed casting.
6. A method of producing a concrete casting as recited in claim 1 , further comprising coating said concrete mold with mold release prior to filling said mold with said aggregate.
7. A method of producing a concrete casting as recited in claim 1 , wherein said coloring dye within said aggregate is an ochre color.
8. A method of producing a concrete casting as recited in claim 1 , wherein after said casting is removed from said concrete mold, said surface of said casting which was formed by said mold base is coated with a sealer.
9. A method of producing a concrete casting as recited in claim 1 , further comprising adjusting the alkalinity of the aggregate to control the amount of carbon dioxide gas produced around said baking soda clumps.
10. A method of producing a concrete casting as recited in claim 1 , further comprising adjusting the volumetric baking powder to water ratio to create a desired size distribution of baking soda clumps.