Carbo-nitriding process for martensitic stainless steel and stainless steel article having improved corrosion resistance
A method for producing a case-hardened martensitic stainless steel article includes: providing an article comprised, at least in part, of a martensitic stainless steel, carburizing the article within a temperature range of 1625° F.-1680° F. (885° C.-916° C.), and then carbo-nitriding the article within a temperature range of 1575° F.-1625° F. (857° C.-885° C.). An article, such as a bearing ring, comprising such a case-hardened martensitic stainless steel is also disclosed.
1. A method comprising:
(a) providing an article comprised, at least in part, of a martensitic stainless steel,
(b) carburizing the article within a temperature range of 1625° F.-1680° F., and
(c) then carbo-nitriding the article within a temperature range of 1575° F.-1625° F., wherein carbon and nitrogen are simultaneously introduced into the case of the stainless steel, thereby producing a case-hardened martensitic stainless steel article,
wherein the martensitic stainless steel in step (a) consists essentially of 0.03-0.10 wt % C, 0.5-1.0 wt % Mn, 0.20-0.6 wt % Si, 11.0-15.0 wt % Cr, 2.40-3.0 wt % Ni, 1.50-2.0 wt % Mo, 0.40-0.80 wt % V, 5.0-6.0 wt % Co, the balance being Fe.
2. A method comprising:
(a) providing a bearing ring comprised, at least in part, of a martensitic stainless steel,
(b) carburizing the bearing ring within a temperature range of 1625° F.-1680° F., and
(c) then carbo-nitriding the bearing ring within a temperature range of 1575° F.-1625° F., wherein carbon and nitrogen are simultaneously introduced into the case of the stainless steel, thereby producing a case-hardened martensitic stainless steel bearing ring,
wherein steps (b) and (c) are performed such that the bearing ring exhibits:
a hard carburized case up to a depth of about 900-1125 μm,
a presence of nitrogen or nitrides up to depth of 250 μm,
0.3-0.7 wt % nitrogen at the surface and 0.1-0.3 wt % nitrogen at a depth of about 250 μm, and
carbon in the range of 1.5-2 wt % in the hardened case, and
wherein the martensitic stainless steel prior to steps (b) and (c) consists of:
0.03-0.10 wt % C, 0.5-1.0 wt % Mn, 0.20-0.6 wt % Si, 12.0-15.0 wt % Cr, 2.40-3.0 wt % Ni, 1.50-2.0 wt % Mo, 0.40-0.80 wt % V, 5.0-6.0 wt % Co, the balance being Fe and unavoidable impurities, and the core of the bearing ring contains the following weight percentages of elements:
Mo+V=0.8 to 4.0 wt % and
Co+Ni=2.0 to 12.0 wt %.
3. A method comprising:
(a) placing an article into a vacuum chamber, the article being comprised of a martensitic stainless steel consisting of 0.03-0.10 wt % C, 0.5-1.0 wt % Mn, 0.20-0.6 wt % Si, 11.0-15.0 wt % Cr, 2.40-3.0 wt % Ni, 1.50-2.0 wt % Mo, 0.40-0.80 wt % V, 5.0-6.0 wt % Co, the balance being Fe and unavoidable impurities,
(b) vacuum carburizing the article within a temperature range of 1625° F.- 1680° F. by repeating a plurality of cycles comprising (i) introducing acetylene into the vacuum chamber and (ii) then evacuating the vacuum chamber to about 0.1 atm, and
(c) then vacuum carbo-nitriding the article within a temperature range of 1575° F.- 1625° F. by repeating a plurality of cycles comprising (i) introducing acetylene and ammonia into the vacuum chamber and (ii) then evacuating the vacuum chamber to about 0.1 atm.