Use of semi-crystalline polymer with low T
The invention provides a method for manufacturing a 3D item ( 10 ) with a fused deposition modeling 3D printer, the method comprising (a) providing a thermoplastic material ( 20 ), wherein the thermoplastic material ( 20 ) comprises a first polymer ( 21 ) of the semi-crystalline type, wherein the first polymer ( 21 ) has a glass temperature (T g ) and wherein the thermoplastic material ( 20 ) has a melting temperature (T m ); generating in a generation stage an intermediate 3D printed item ( 110 ) by printing the thermoplastic material ( 20 ), wherein the thermoplastic material ( 20 ) is heated to a temperature equal to or above the melting temperature (T m ), while maintaining during printing an ambient temperature (T a ) to the intermediate 3D printed item under construction below the glass temperature (T g ); and generating in an annealing stage said 3D item ( 10 ) by heating the intermediate 3D printed item ( 110 ) equal to or above the glass temperature (T g ).
1. A method for manufacturing a 3D item with a fused deposition modeling 3D printer, the method comprising:
providing a thermoplastic material comprising (a) a first polymer having a mass fraction of at least 90%, and (b) an additive having a mass fraction of 0-6%, wherein the first polymer is a semi-crystalline aromatic polyester;
generating in a generation stage an intermediate 3D printed item by printing the thermoplastic material, wherein the thermoplastic material is heated to a temperature equal to or above a melting temperature (Tm) of the thermoplastic material, while maintaining during printing an ambient temperature (Ta) of the 3D printed item under construction below the glass temperature (T g ) of the first polymer; and
generating in an annealing stage said 3D item by heating the intermediate 3D printed item to a temperature equal to or above the glass temperature (T g ) of the first polymer,
wherein the method further comprises a design stage, comprising determining dimensions of the 3D item and defining dimensions of the intermediate 3D printed item taking into account a shrinkage during the annealing stage.
2. The method according to claim 1 , wherein the fused deposition modeling 3D printer comprises a receiver item, and wherein the method further comprises maintaining the receiver item during at least part of the generation stage at a temperature below the glass temperature (T g ) of the first polymer.
3. The method according to claim 1 , wherein the fused deposition modeling 3D printer comprises a printing chamber within which the generation stage is executed, and wherein the method further comprises maintaining the printing chamber during at least part of the generation stage below the glass temperature (T g ) of the first polymer.
4. The method according to claim 3 , wherein the method comprises heating the printing chamber during at least part of the annealing stage at a temperature equal to or above the glass temperature (T g ) of the first polymer.
5. The method according to claim 1 , wherein the method comprises heating the intermediate 3D printed item to a temperature equal to or above the glass temperature (T g ) of the first polymer until the first polymer obtains a degree of crystallinity of at least 20%.
6. The method according to claim 1 , wherein the additive has a mass fraction of 0-1% of the additive and wherein the first polymer has a mass fraction of at least 95%, relative to the total weight of the thermoplastic material.
7. The method according to claim 6 , wherein the additive comprises one or more of a colorant, a luminescent material, and a reflective material.
8. The method according to claim 1 , wherein the first polymer has a glass temperature (T g ) below 120° C. and a melting temperature (Tm) of at least 150° C.
9. The method according to claim 1 , wherein the first polymer has a melting temperature (Tm) of at least 200° C.
10. The method according to claim 1 , wherein the semi-crystalline aromatic polyester is polyethylene terephthalate (PET).