Doped materials/alloys and hot isostatic pressing method of making same
View Patent ↗A method of forming a doped substrate comprises heating a substrate comprising a layer of a dopant on at least one surface to a predetermined temperature; applying a predetermined degree of isostatic external pressure on the surface of said substrate at said predetermined temperature for a time sufficient to induce thermal migration of the dopant into the substrate to provide a doped substrate; and removing the isostatic pressure and cooling the doped substrate to about room temperature. The substrate is a glass material, a single crystal material, a poly-crystalline material, a ceramic material, or a semiconductor material, and the substrate may be optically transparent. The dopant comprises one or more transition metals, one or more rare earth elements, or a combination of both. The layer of a dopant comprises one or more segregated layers of distinct chemical species. The isostatic pressure and elevated temperature may be applied simultaneously or sequentially.
1. A method of forming a doped substrate, comprising:
(a) heating a substrate comprising a layer of a dopant on at least one surface to a predetermined temperature;
(b) applying a predetermined degree of isostatic external pressure on the at least one surface of said substrate at said predetermined temperature for a time sufficient to induce migration of the dopant into the substrate to provide a doped substrate; and
(c) removing the isostatic pressure and cooling the doped substrate to about room temperature,
wherein the substrate is selected from the group consisting of Yttrium Lithium Fluoride (YLF), Yttrium orthovanadate (Nd:YVO 4 ), Neodymium doped yttrium calcium oxoborate Nd:YCa 4 O(BO 3 ) 3 , lithium strontium (or calcium) aluminum fluoride (Ce:LiSAF, Ce:LiCAF), chrysoberyl (alexandrite), Gallium Nitride (GaN), Indium Gallium Nitride (InGaN), Aluminum Gallium Indium Nitride (InGaInP), Aluminum Gallium Arsenide Phosphide (InGaAsP), Lithium niobate (LiNbO 3 ), Potassium Niobate (KNbO 3 ), Strontium Barium Niobate (SBN), Yttrium Scandium Gallium Garnet (YSGG), Yttrium Vanadate (YVO 4 ), Terbium Gallium Garnet (Tb 3 Ga 5 O 12 ), Potassium Gadolinium Tungstate (KGW), Forsterite (Mg 2 SiO 4 ), Barium Yttrium Fluoride (BaY 2 F 5 ), Barium Yttrium Lutetium Fluoride (BaYLuF 5 ), and combinations thereof,
wherein the dopant is one or more atomic or ionic species of elements selected from the group consisting of gold, iridium, molybdenum, niobium, palladium, rhenium, rhodium, ruthenium, titanium, tungsten, lanthanum, praseodymium, europium, gadolinium, lutetium, or combinations thereof.
2. The method of claim 1 , wherein the substrate is optically transparent.
3. The method of claim 1 , wherein the layer of a dopant comprises one or more segregated layers of distinct chemical species, a plurality of blended dopant materials, or a plurality of dopant materials as a eutectic.
4. The method of claim 1 , wherein the predetermined temperature is between about 100° C. to about 2,500° C.
5. The method of claim 1 , wherein the degree of isostatic pressure is between about 1,000 PSI to about 250,000 PSI.
6. The method of claim 1 , wherein the time sufficient to induce migration of the dopant into the substrate is between about 1 hour to about 1,000 hours.
7. The method of claim 1 , wherein a thickness of the layer of dopant is within a range from about 60 Å to about 60,000 Å.
8. The method of claim 1 , wherein heating the substrate and applying the degree of isostatic pressure is performed in an inert atmosphere.
9. The method of claim 1 , wherein heating the substrate and applying the degree of isostatic external pressure is performed in an atmosphere comprising Carbon Dioxide, Neon, Helium, or combinations thereof.