Laser-welded shaped steel and method for producing same
A laser-welded shape section steel includes a web member and a flange member each made of a steel plate, the steel plate having an equivalent carbon content C eql of not less than 0.075 and not more than 0.15, the equivalent carbon content C eql being represented by the following formula: C eql =C+(Si/50)+(Mn/25)+(P/2)+(Cr/25)+Ti, where a welded part, which is a joint part in which the web member and the flange member are joined, has a hardness of not less than 1.2 times and not more than 4 times as hard as that of the steel plate, and the welded part a protrusion length of not greater than 1 mm.
1. A laser-welded section shape steel, comprising:
a web member and a flange member each made of a steel plate,
the laser-welded section shape steel satisfying the following conditions (a) and (b):
(a) the steel plate of the web member and the steel plate of the flange member each having an equivalent carbon content C eql of not less than 0.075 and not more than 0.15, the equivalent carbon content C eql being represented by following Formula (1) in which each element represents a weight percentage:
C
eql
=
C
+
Si
50
+
Mn
25
+
P
2
+
Cr
25
+
Ti
;
(
1
)
and
(b) a welded part, which is a joint part in which the web member and the flange member are joined, having a hardness of not less than 2.8 times and not more than 4 times as hard as an average hardness of the steel plate of the web member and of the steel plate of the flange member,
lengths α, β, γ, and δ being not greater than 1 mm, where (i) a side of the web member, which side has been irradiated with laser light, is referred to as a front side, (ii) the welded part protrudes, by the length α, from the flange member on the front side of the web member, (iii) the welded part protrudes, by the length γ, from the front side of the web member, (iv) the welded part protrudes, by the length β, from the flange member on a back side of the web member, and (v) the welded part protrudes, by the length δ, from the back side of the web member.
2. The laser-welded section shape steel as set forth in claim 1 , wherein:
the web member has a thickness of not greater than 6 mm.
3. A method of producing a laser-welded section shape steel including a web member and a flange member each made of a steel plate, the method comprising the step of:
joining the web member to the flange member by carrying out laser welding,
the laser-welded section shape steel satisfying the following conditions (a) and (b):
(a) the steel plate of the web member and the steel plate of the flange member each having an equivalent carbon content C eql of not less than 0.075 and not more than 0.15, the equivalent carbon content C eql being represented by following Formula (1) in which each element represents a weight percentage:
C
eql
=
C
+
Si
50
+
Mn
25
+
P
2
+
Cr
25
+
Ti
;
(
1
)
and
(b) a welded part, which is a joint part in which the web member and the flange member are joined, having a hardness of not less than 2.8 times and not more than 4 times as hard as an average hardness of the steel plate of the web member and of the steel plate of the flange member, and
lengths α, β, γ, and δ being not greater than 1 mm, where (i) a side of the web member, which side has been irradiated with laser light, is referred to as a front side, (ii) the welded part protrudes, by the length α, from the flange member on the front side of the web member, (iii) the welded part protrudes, by the length γ, from the front side of the web member, (iv) the welded part protrudes, by the length β, from the flange member on a back side of the web member, and (v) the welded part protrudes, by the length δ, from the back side of the web member.