Composite polymer electrolyte membrane, membrane electrode assembly and solid polymer fuel cell using same
A composite polymer electrolyte membrane has a high proton conductivity even under low-humidity, low-temperature conditions, a reduced dimensional change rate, a high mechanical strength and high chemical stability, and produces a solid polymer electrolyte fuel cell with a high output and high physical durability, a membrane electrode assembly, and a solid polymer electrolyte fuel cell containing the same. This composite polymer electrolyte membrane contains a composite layer composed mainly of a polyazole-containing nanofiber nonwoven fabric (A) and an ionic group-containing polymer electrolyte (B), the polyazole-containing nanofiber nonwoven fabric (A) being basic.
1. A composite polymer electrolyte membrane comprising a composite layer composed mainly of a polyazole-containing nanofiber nonwoven fabric (A) and an ionic group-containing polymer electrolyte (B), the polyazole-containing nanofiber nonwoven fabric (A) being basic, and
wherein the polyazole-containing nanofiber nonwoven fabric (A), examined by emission spectrum analysis, shows a ratio (I450/I300) of 0.30 or more and 1.4 or less, and I450 and I300 are the peak intensities determined under excitation at 450 nm and 300 nm, respectively.
2. The composite polymer electrolyte membrane as set forth in claim 1 , wherein the polyazole-containing nanofiber nonwoven fabric (A) is a polybenzazole based nanofiber nonwoven fabric.
3. The composite polymer electrolyte membrane as set forth in claim 1 , wherein the polyazole-containing nanofiber nonwoven fabric (A) is a nanofiber nonwoven fabric containing polybenzimidazole fibers.
4. The composite polymer electrolyte membrane as set forth in claim 1 , wherein polyazole accounts for 80 wt % or more of the polyazole-containing nanofiber nonwoven fabric (A).
5. The composite polymer electrolyte membrane as set forth claim 1 , wherein the polyazole-containing nanofiber nonwoven fabric (A) shows a weight change rate of 50% or less after staying in N-methyl-2-pyrolidone at 30° C. for 1 hour.
6. The composite polymer electrolyte membrane as set forth in claim 1 , wherein the ionic group-containing polymer electrolyte (B) is an ionic group-containing aromatic hydrocarbon based polymer.
7. The composite polymer electrolyte membrane as set forth in claim 1 , wherein the ionic group-containing polymer electrolyte (B) is a block copolymer comprising at least one ionic group-containing segment (B 1 ) and at least one ionic group-free segment (B 2 ).
8. The composite polymer electrolyte membrane as set forth in claim 7 , wherein the ionic group-containing polymer electrolyte (B) forms a co-continuous type phase separated structure.
9. A catalyst coated membrane comprising a catalyst layer formed on the composite polymer electrolyte membrane as set forth in claim 1 .
10. A membrane electrode assembly comprising the composite polymer electrolyte membrane as set forth in claim 1 .
11. A solid polymer electrolyte fuel cell comprising the composite polymer electrolyte membrane as set forth in claim 1 .
12. An electrochemical hydrogen pump comprising the composite polymer electrolyte membrane as set forth in claim 1 .
13. Water electrolysis hydrogen generation equipment comprising the composite polymer electrolyte membrane as set forth in claim 1 .
14. A polyazole-containing nanofiber nonwoven fabric that, when examined by emission spectrum analysis, has a ratio (I450/I300) of 0.30 or more and 1.4 or less wherein I450 and I300 are the peak intensities determined under excitation at 450 nm and 300 nm, respectively.
15. The polyazole-containing nanofiber nonwoven fabric as set forth in claim 14 having a polyazole content of 80 wt % or more and a weight change rate of 50% or less after contact with N-methyl-2-pyrolidone at 30° C. for 1 hour.
16. A method of producing polyazole-containing nanofiber nonwoven fabric that, when examined by emission spectrum analysis, shows a ratio (I450/I300) of 0.30 or more and 1.4 or less, and I450 and I300 are the peak intensities determined under excitation at 450 nm and 300 nm, respectively, comprising:
step 1 dissolving polymers used as materials for the polyazole-containing nanofiber nonwoven fabric,
step 2 producing a nanofiber nonwoven fabric precursor by electrospinning of the solution resulting from step 1, and
step 3 performing insolubilization treatment of the nanofiber nonwoven fabric precursor resulting from step 2.
17. The method as set forth in claim 16 , wherein the insolubilization treatment in step 3 comprises heat treatment at a temperature T(° C.) that meets equation (F1):
Tg 1−50(° C.)≤ T≤Tg 1+20(° C.) (F1)
wherein Tg1 denotes the glass transition temperature (° C.) of the polyazole contained in the polyazole-containing nanofiber nonwoven fabric.
18. The method as set forth in claim 16 , wherein the insolubilization treatment in step 3 comprises heat treatment performed after spreading a polyazole-containing nanofiber nonwoven fabric on a base having a glass transition temperature Tg2 (° C.) meeting equation (F2) and/or a melting point Tm (° C.):
Tg 2( Tm )> T (F2)
wherein, Tg2 is the glass transition temperature (° C.) of the substance of the base and Tm(° C.) is the melting point of the substance of the base.