Exhaust gas-purifying composition
An exhaust gas purifying composition of the present invention contains zeolite that is BEA zeolite having an SiO 2 /Al 2 O 3 molar ratio of greater than 25 and 600 or less and containing phosphorus. Furthermore, the exhaust gas purifying composition preferably contains zirconium in addition to phosphorus. Furthermore, the zeolite has an SiO 2 /Al 2 O 3 molar ratio of from 30 to 150. The present invention provides an exhaust gas purifying composition having excellent HC adsorbability for exhaust gas purification in internal combustion engines such as gasoline engines.
1. An exhaust gas purification method comprising purifying exhaust gas emitted from a gasoline engine by using a composition comprising BEA zeolite which has an SiO 2 /Al 2 O 3 molar ratio of greater than 25 and 600 or less and which contains phosphorus and zirconium, wherein an amount of the phosphorus contained in the zeolite is such that a molar ratio (P/Al) thereof with respect to Al in the BEA zeolite is 0.5 or greater, an amount of the zirconium contained in the zeolite is such that a molar ratio (Zr/Al) thereof with respect to Al in the zeolite is 0.5 or greater, and the BEA zeolite which contains phosphorus and zirconium has a Zr—O—P bond.
2. The exhaust gas purification method according to claim 1 , wherein hydrocarbon contained in exhaust gas emitted into an exhaust passage of the gasoline engine is removed.
3. The exhaust gas purification method according to claim 1 , wherein the zeolite has an SiO 2 /Al 2 O 3 molar ratio of from 30 to 150.
4. The exhaust gas purification method according to claim 1 , wherein an amount of the zirconium contained in the zeolite is such that a molar ratio (Zr/Al) thereof with respect to Al in the zeolite is from 0.5 to 4.
5. The exhaust gas purification method according to claim 1 , wherein the zeolite has an SiO 2 /Al 2 O 3 molar ratio of from 30 to 150, and an amount of the phosphorus contained in the zeolite is such that a molar ratio (P/Al) thereof with respect to Al in the BEA zeolite is from 1 to 3.
6. The exhaust gas purification method according to claim 1 , wherein a specific surface area maintaining factor represented by A/B×100(%) is 35% or greater, where A represents a specific surface area after heating at 980° C. for 25 hours, and B represents a specific surface area before heating.
7. The exhaust gas purification method according to claim 1 , wherein the composition is a fired material of a mixture of BEA zeolite and a dispersion or solution containing phosphoric acid or salts thereof and a water-soluble zirconium salt.
8. An exhaust gas purification method according to claim 1 , comprising purifying exhaust gas emitted from a gasoline engine by using a composition comprising BEA zeolite which has an SiO 2 /Al 2 O 3 molar ratio of greater than 25 and 600 or less and which contains phosphorus and zirconium, wherein an amount of the phosphorus contained in the zeolite is such that a molar ratio (P/AI) thereof with respect to Al in the BEA zeolite is 0.5 or greater, an amount of the zirconium contained in the zeolite is such that a molar ratio (Zr/AI) thereof with respect to Al in the zeolite is 0.5 or greater and 2 or less, and a peak is observed in a range of −21 to −29 ppm in P-NMR measurement of the composition.