Polyethylene resin having excellent impact strength
The present invention relates to polyethylene resin having excellent impact strength, and more specifically, to polyethylene resin exhibiting excellent impact strength and flexural strength, when prepared into a molded product.
1. Polyethylene resin comprising ethylene polymer or (co)polymer of ethylene and alpha olefin, and having a spreading gradient value of 5 to 10 (×10 6 Pa/m),
wherein the spreading gradient value means an average gradient between a minimum point and a second maximum point in a stress-strain curve, measured by ASTM D 638,
wherein the minimum point is a point where strain begins again according to stress increase after passing a yield point in a stress-strain curve, measured by ASTM D 638, and
wherein the second maximum point is a point where ultimate tensile strength (UTS) is reached in a stress-strain curve, measured by ASTM D 638.
2. The polyethylene resin according to claim 1 , wherein the polyethylene resin has a complex modulus value is of 10 to 17 (×10 8 Pa).
3. The polyethylene resin according to claim 1 , wherein the polyethylene resin satisfies the following Mathematical Formula 1:
( X−a ) 2 +( Y−b ) 2 ≤25 [Mathematical Formula 1]
in the Mathematical Formula 1,
X means a spreading gradient value(×10 6 Pa/m),
Y means a complex modulus value(×10 8 Pa),
a is 5 to 10, and b is 14 to 16.
4. The polyethylene resin according to claim 1 , wherein the polyethylene resin has a melt flow index (MI) measured by ASTM D 1238 of 5 to 10 g/10 minutes.
5. The polyethylene resin according to claim 1 , wherein the polyethylene resin has a melt flow rate ratio under load (MI 5 /MI 2.16 , MFRR) measured by ASTM D 1238 of 3 to 4.
6. The polyethylene resin according to claim 1 , wherein the polyethylene resin has a density value measured by ASTM D 792 of 0.950 to 0.970 g/cm 3 .
7. The polyethylene resin according to claim 1 , wherein the polyethylene resin has a flexural strength value measured by ASTM D 790 of 11,000 kgf/cm 2 or more.
8. The polyethylene resin according to claim 1 , wherein the polyethylene resin has a spiral flow value measured by ASTM D 3123 of 16 cm or more.
9. A polyethylene resin molded product comprising the polyethylene resin according to claim 1 .