Separation membranes
A process for the preparation of ultrafiltration and microfiltration polymeric flat sheet separation membranes is disclosed, the process comprising a unidirectional cooling step. Membranes prepared according to the process exhibit numerous advantages over ultrafiltration and microfiltration membranes prepared via conventional processes. In particular, the membranes prepared by the present process exhibit remarkable pure water flux, superior mechanical properties and increased anti-fouling characteristics. Also disclosed are particular PVDF ultrafiltration and microfiltration membranes having improved flux, mechanical and anti-fouling properties.
1. A process for the preparation of a flat sheet polymeric membrane having an average pore size of 0.01-10 μm, the process comprising the steps of:
a) providing a polymeric dope solution comprising a polymer and a first solvent, wherein:
i) the polymer is poly(vinylidene fluoride), poly(ethersulfone) or cellulose acetate and the first solvent is dimethyl sulfoxide, or
ii) the polymer is cellulose acetate and the first solvent is acetic acid;
b) casting the polymeric dope solution onto a substrate to form a cast polymeric film, the cast polymeric film having a first surface being in contact with the substrate, and a second surface disposed opposite the first surface;
c) subjecting the cast polymeric film to a cooling means, the cooling means being provided at a temperature that is 5-120° C. below the melting temperature of the first solvent; and
d) contacting the cooled cast polymeric film resulting from step c) with a second solvent, the second solvent being provided at a temperature below the melting point of the first solvent, and the second solvent being miscible with the first solvent;
wherein during step c) only one of the first and second surfaces of the cast polymeric film is subjected to the cooling means, and
wherein step d) removes the first solvent in a frozen state from the cast polymeric film.
2. The process of claim 1 , wherein the polymer is poly(vinylidene fluoride) or poly(ethersulfone) and the first solvent is dimethyl sulfoxide.
3. The process of claim 1 , wherein the polymer is poly(vinylidene fluoride) the first solvent is dimethyl sulfoxide.
4. The process of claim 1 , wherein the dope polymeric solution comprises 10-30 wt % of the polymer.
5. The process of claim 1 , wherein step b) comprises casting the polymeric dope solution onto a substrate to form a cast polymeric film having an average thickness of 0.05-2 mm.
6. The process of claim 1 , wherein the cooling means is provided at a temperature that is 15-100° C. below the melting temperature of the first solvent.
7. The process of claim 1 , wherein step c) comprises subjecting the first surface of the cast polymeric film to the cooling means.
8. The process of claim 1 , wherein the substrate is sheet-like, having a first surface being in contact with the cast polymeric film, and a second surface disposed opposite the first surface.
9. The process of claim 8 , wherein step c) comprises subjecting the second surface of the substrate to the cooling means.
10. The process of claim 1 , wherein the substrate is glass or is metalli.
11. The process of claim 1 , wherein the substrate has an average thickness of 2-15 mm.
12. The process of claim 1 , wherein the cooling means is a sheet-like structure.
13. The process of claim 1 , wherein the polymeric dope solution further comprises at least one dopant suitable for increasing the hydrophilicity of the membrane.
14. The process of claim 13 , wherein the weight ratio of polymer to dopant within the polymeric dope solution is 2:1 to 8:1.
15. The process of claim 1 , wherein:
i) the flat sheet polymeric membrane has an average pore size of 0.01-1.5 μm;
ii) the cooling means in step c) is a sheet-like structure or a liquid, and is provided at a temperature that is 40-80° C. below the melting temperature of the first solvent; and
iii) step c) comprises subjecting only the first surface of the cast polymeric film to the cooling means by applying the cooling means to the second surface of the substrate.
16. The process of claim 3 , wherein:
i) the flat sheet polymeric membrane has an average pore size of 0.01-1.5 μm;
ii) in step b), the substrate has a thickness of 2-20 mm and the polymeric dope solution is cast onto the substrate to form a cast polymeric film having a thickness of 0.05-2 mm;
iii) the cooling means in step c) is a plate formed from a metal or glass, and is provided at a temperature that is 40-80° C. below the melting temperature of the first solvent; and
iv) step c) comprises subjecting only the first surface of the cast polymeric film to the cooling means by applying the cooling means to the second surface of the substrate.
17. The process of claim 1 , wherein the second solvent is water.
18. The process of claim 1 , wherein the cooling means is provided at a temperature of −18 to −50° C.
19. The process of claim 13 , wherein the at least one dopant is poly(ethylene glycol).