Composition for hydrolytic stabilization of polyester
The invention relates to the use of at least one compound of the formula (1) wherein R 1 and R 2 are the same or different and denote a C 1 -C 10 -alkyl as a hydrolysis stabilizer in polyester materials.
1. A method of stabilization of polyester materials against hydrolysis said method being characterized by adding at least one compound of the formula (1)
wherein
R 1 and R 2 are the same or different and denote a C 1 -C 10 -alkyl,
as a hydrolysis stabilizer in said polyester materials, and
wherein the compound of formula (1) is in a proportion of from 0.1 to 20.0 wt.-%, based on the weight of a proportion of the stabilized polyester materials.
2. The method as claimed in claim 1 , wherein the compounds of the formula (1) are dimethylterephthalate, diethylterephthalate, dipropylterephthalate, dibutyl-terephthalate, dipentylterephthalate, dihexylterephthalate, diheptylterephthalate, dioctylterephthalate, dinonylterephthalate or didecylterephthalate.
3. The method as claimed in claim 1 , wherein the compound of formula (1) is dimethylterephthalate.
4. The method as claimed in claim 1 , wherein the polyester in the polyester materials is polyethylene terephthalate, polyethylene naphthalate, polybutylene terephthalate, polytrimethylene terephthalate, dibenzoyl polyethylene terephthalate, dibenzoyl polybutylene terephthalate, dibenzoyl polyethylene naphthalate or mixtures thereof.
5. The method as claimed in claim 1 , wherein the polyester in the polyester materials is polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate and polytrimethylene terephthalate, and mixtures and co-polyesters thereof.
6. The method as claimed in claim 1 , wherein the polyester in the polyester materials are aliphatic polyesters selected from the group consisting of polyhydroxybutyrate and its copolymer with polyhydroxyvalerate, polyhydroxybutyrate-valerate, poly (ε-caprolactone).
7. The method as claimed in claim 1 , further comprising forming the polyester materials in to a stretched film.
8. The method as claimed in claim 1 , wherein the proportion of the compound of formula (1) is from 1.0 to 10.0 wt.-%, based on the weight of the stabilized polyester material.
9. The method as claimed in claim 1 , wherein the proportion of the compound of formula (1) is from 1.5 to 5.0 wt.-%, based on the weight of the stabilized polyester material.
10. The method as claimed in claim 1 , wherein the compound of formula (1) is added in combination with further additives selected from the group consisting of radical scavengers, light stabilizers, heat stabilizers, flame retardants, pigments, dyes, antioxidants, antibacterial agents, neutralizers, antistatic agents, antiblocking agents, optical brighteners, heavy metal inactivation agents, hydrophobic agents, peroxides, water scavengers, acid scavengers, hydrotalcites, elastomers, impact modifiers, laser marking additives, processing aids, and mixtures thereof.
11. The method as claimed in claim 1 , wherein the compound of formula (1) is added in combination with UV-absorbers.
12. The method as claimed in claim 1 , further comprising dispersing the compound of formula (1) in a carrier material to form a masterbatch and adding the masterbatch to said polyester materials.
13. The method as claimed in claim 1 , wherein the polyester material is in the form of a film or a sheet.